Electronics Forum | Mon Oct 25 15:56:56 EDT 1999 | Dave F
William: Three things: 1 If the gold is porous, it will not protect the nickel and the nichel wiil oxidize and become unsolderable. 2 If the nickel is not solderable, the gold overcoat will not improve that. 3 Ag or Au over electroless Ni creates b
Electronics Forum | Fri Sep 20 01:39:21 EDT 2013 | winson16
gold, one of the stablest elements on the > periodic table oxidising. Are you sure, and why > would you want to reduce the vision fail rate on > a part that is clearly shockingly poor? Old inventory is holding a huge material cost and if i can f
Electronics Forum | Tue Sep 03 22:32:04 EDT 2002 | davef
Naw, alcohol and solvents won't do dip. Hold-off on: * Destructive testing. [Athough this will convince you to move on to other things.] * Rework of the solder connections. [Although this will correct the problem.] Consider investigating your aque
Electronics Forum | Fri Mar 14 11:04:54 EDT 2008 | herman
Samir, To correct some misconceptions on the answers to your question, and "what you know from experience": With both ENIG (Electroless Nickel/Immersion Gold-IAu) and IAg (immersion silver), soldering does not take place to the gold or the silver. Wh
Electronics Forum | Sat Feb 20 09:41:51 EST 1999 | Andy
| We are using .040" diameter fiducials (global and local) on our boards. They are solder covered and HASL. I get batches of boards where the p&p vision system has trouble reading the fiducial. The fiducial looks dark on the screen. The board ven
Electronics Forum | Tue Nov 14 21:27:26 EST 2006 | davef
"Hidden pillow" seems to be a a variant of "pillow effect" or "head in pillow". Pillow effect is an open, with non-wetting between the lead and the solder on the pad. Here the lead sags into the solder without any bonding or wetting. Poor wetting c
Electronics Forum | Fri Aug 20 14:22:02 EDT 1999 | Earl Moon
| | | I am being asked, by my vendor and Purchasing people about converting from Tin/lead pads on P.C.B's to Electroless Tin Plating. | | | Can any one tell me what I have to change in my SMT | | | process (paste, reflow, etc) If any? | | | I
Electronics Forum | Fri Aug 20 12:18:11 EDT 1999 | Earl Moon
| I am being asked, by my vendor and Purchasing people about converting from Tin/lead pads on P.C.B's to Electroless Tin Plating. | Can any one tell me what I have to change in my SMT | process (paste, reflow, etc) If any? | I ran one P.C.Boar
Electronics Forum | Fri Aug 20 12:54:11 EDT 1999 | Carol Zhang
| | I am being asked, by my vendor and Purchasing people about converting from Tin/lead pads on P.C.B's to Electroless Tin Plating. | | Can any one tell me what I have to change in my SMT | | process (paste, reflow, etc) If any? | | I ran one
Electronics Forum | Mon Sep 13 06:23:06 EDT 1999 | Earl Moon
| | We have a product, with various PWBs, with over 600 parts each one (We are a low Volume/high mix company with an average component placement per PCB between 250 to 300 parts). This PWBs have 7 to 10, 20 mils pitch parts. We are having problems wi