Electronics Forum | Mon Nov 05 13:33:08 EST 2007 | slthomas
Heck no, I mean we print relatively slower on complex boards, as in 1 inch/sec (25.4mm/sec), and maybe 2 inches/sec. (51mm/sec) on less complex boards. SMT is not a bottleneck in our plant and printing never the bottleneck in SMT, so I see no need t
Electronics Forum | Mon May 30 09:11:15 EDT 2011 | davef
3a ANSI/J-STD-001: * Temperature and Humidity: 18-30°C, 30-70%RH ** If out of range, shall verify electrostatic discharge control program according to ANSI/ESD S20-20 is adequate. ** For process control, more restrictive temperature and humidity lim
Electronics Forum | Mon Nov 05 16:54:00 EST 2007 | bbarton
There are several things that can be done to increase throughput on you screen printer, including the panelization of your bords as Steve & Hussman has pointed out. However that's of limited use if you have plenty of stock that is not panelized. That
Electronics Forum | Thu Mar 02 13:13:14 EST 2006 | Chunks
A ballast is the device needed to energize fluorescent lamps during operation. In all fluorescent lighting systems, the ballast provides the proper voltage to start the lamp and then regulates the electric current flowing through the lamp to stabiliz
Electronics Forum | Thu Jan 12 10:05:13 EST 2006 | davef
There's a lots comparisons like this on the web. Here's one: Westwood Associates said on 8/12/2003: ||HASL||OSP||ENIG||Pd||Tin||Silver Flat||no||yes||yes||yes||yes||yes Solderjoint||Cu-Sn||Cu-Sn||Ni-Sn||Ni-Sn||Cu-Sn||Cu-Sn Contact||E-test, ICT||no|
Electronics Forum | Sat Nov 17 12:58:12 EST 2007 | mika
I agree with previous postings regarding print speed: Solder paste type/versus fine pitch. Question: Is this a double sided pcb with fairly easy component packages on both sides? In such case, consider make the panel like this: Every second pcb in
Electronics Forum | Thu Feb 10 00:42:24 EST 2011 | lenne
nobody can reply me?i just wanna know what is the base material of producing the film.exclude the material,what else should i get to know?
Electronics Forum | Wed Dec 07 00:44:31 EST 2005 | arnold
were having a problem on the units after soldered. after few hours or days the soldered wires has green decay. what does it cause. how can i prevent this.
Electronics Forum | Wed Dec 07 11:54:37 EST 2005 | russ
Would you by chance be soldering copper to aluminum?
Electronics Forum | Mon Dec 26 23:19:29 EST 2005 | arnold
is there any term called on that corrosion or green contamination?