Electronics Forum | Thu Nov 11 10:55:32 EST 1999 | KenF
Hi, could anyone tell me the maximum size of an SMD ceramic capacitor that can be assembled on a copper based substrate reliably? The SMD will be reflowed on the copper substrate. The main concern is the CTE mismatch between the ceramic capacitor and
Electronics Forum | Mon Feb 27 06:42:37 EST 2006 | Slaine
What are the long term issues with high tin content solders on parts plated with silver over copper? Is it possible that the silver will be absorbed by the solder then over a long period of time the tin will react with the copper causing it to part
Electronics Forum | Mon Feb 27 09:31:10 EST 2006 | Slaine
on sections ive looked at with 7 microns of silver and 4microns of copper, the silver had been totally absorbed into the solder in most places and a large amount in some places all the copper as well, so i think the answer is that to provide long ter
Electronics Forum | Thu Oct 16 11:15:53 EDT 2008 | davef
A good solder connection with heavy ground plane requires: * Plenty of heat [Is the preheater located too far from the wave? Whenever you look at board temperature, there is a sharp decrease in temperature between the preheater and the wave.] * Conta
Electronics Forum | Fri Aug 17 01:40:55 EDT 2001 | V.RAMANAND KINI
We are in the watch & clock Business. We have a Watch IC chip that has to be wirebonded using Ultrasonic aluminium wedge bonder. The wire dia is 1.25mil. The PCB is made of G10 Glass epoxy copper clad laminate. The copper thickness is 18 microns. The
Electronics Forum | Thu Jul 06 20:17:25 EDT 2000 | Dave F
KC: I can't find it either ... I know I'm just rushin too much to concentrate on it. But yano even if it isn't in A-600, it doesn't make sense that you fab should be able to add copper without your approval.
Electronics Forum | Wed Jun 22 09:42:51 EDT 2005 | davef
Not sure what a higher Tg laminate will accomplish. Can't hurt though. Remember, when soldering to Alloy 42, the surface is 42% nickel. So, you need to raise the reflow temperature some 15 to 20*C over what is needed for copper. Also, sometimes All
Electronics Forum | Thu Apr 20 02:27:11 EDT 2017 | pavel_murtishev
Mile, Please tell me more about your soldering process: - Are soldering process parameters the same for all three pins? - Is unsoldered pin connected to thermal heavy copper polygon? - What is your board surface finish? HASL? - Sn/Pb or LF process?
Electronics Forum | Fri Jul 07 09:15:23 EDT 2000 | K. Chak
Hi Dave, This particular p/n calls for print&etch for wet process..and the problem occured due to surface contamin. with resist residue resisting copper from etching off. The high pressure nozzle was a problem at developing oper. and it is fixed now
Electronics Forum | Tue Aug 07 21:17:24 EDT 2001 | davef
This provides LT 3 misses /1M hits. * Probe all points on one side of the board. Bonus => This lower fixture cost. * Test pads and vias: GT 25 thou from other land traces. * Small [LT 5 ohm] resistor measurements: Use two pads at each end and do 4-