Electronics Forum | Mon Jul 01 15:37:56 EDT 2002 | pjc
Possible cause can be design related- if the solder land is too small. Check w/ IPC SM-782 Solder Land Design Guide Another is board finish. I have seen problems like this with Gold finished PWBs- which creates a more brittle solder joint.Another pos
Electronics Forum | Tue Feb 02 12:31:26 EST 1999 | John
| I have a product using high temperature solder to connect terminal pins to a PCB. The board is single sided copper, no plaiting. The solder is 95% tin 5 % silver. The flux is low activity rosin. The product is a subassembly. When the product i
Electronics Forum | Mon Feb 01 16:40:45 EST 1999 | Dave Waddick
I have a product using high temperature solder to connect terminal pins to a PCB. The board is single sided copper, no plaiting. The solder is 95% tin 5 % silver. The flux is low activity rosin. The product is a subassembly. When the product is
Electronics Forum | Fri Jul 12 22:15:56 EDT 2013 | ericrr
Sorry to build up your hopes. The latest thing to hit the air ways at work, I was accessed of fiddling with the oven settings, because there were reports of "cracked joints" there was no mention of where the cracks were, cracked at the pcb or cracke
Electronics Forum | Fri Dec 14 13:58:07 EST 2001 | slthomas
This is one I haven't seen before (not in this context, anyway). We have an assembly that we have the SMT done out of house on, because of the high volumes. The boards have two distinct characteristics with respect to the appearance of the solder jo
Electronics Forum | Tue Nov 13 21:59:42 EST 2007 | davef
This processes has the potential to cause barrel cracking and pad lifting, because the heating is very hot [troop crank-up the volume on their iron when they see thick boards] for a relatively small area on one side of the board. What do we suggest
Electronics Forum | Tue Jun 25 09:45:39 EDT 2019 | edhare
See also ... https://www.semlab.com/solder-joint-failure-modes/
Electronics Forum | Fri May 31 05:54:09 EDT 2019 | dhanish
What are the common cause for solder joint crack after the pcba go through Temperature cycling test ?We have seen failure on solder joint for the memory part.
Electronics Forum | Sat Jun 01 04:22:24 EDT 2019 | gregoryyork
Depends on lead free alloy choice as well