Electronics Forum | Sun Apr 11 11:39:52 EDT 2010 | manchella
When we have sent some of motherboards for reliability testing in a tird party laoratory. It is found that when Dye&Pry is done after 600 cycles of Thermal Cycling, in LGA socket only one of the corner solder joing had 100% type 3 crack. All other so
Electronics Forum | Tue Jun 07 16:19:58 EDT 2005 | davef
Q1) How to identify on good or bad ICs lead that could contribute to dewetting? A1) Distinguish between good or bad IC that could contribute to dewetting by testing for solderability, according to J-STD-002. Q2) What actions that must be taken in fa
Industry News | 2016-04-06 12:45:01.0
The SMTA is excited to announce three new workshops for the 10th Annual International Conference on Soldering and Reliability (ICSR) being held May 9-11, 2016 in Toronto, Canada. The event is co-located with the SMTA Toronto Expo.
Industry News | 2016-04-07 09:04:01.0
The SMTA is excited to announce three new workshops for the 10th Annual International Conference on Soldering and Reliability (ICSR) being held May 9-11, 2016 in Toronto, Canada. The event is co-located with the SMTA Toronto Expo.
Technical Library | 2015-02-19 16:54:34.0
Pad cratering is an important failure mode besides crack of solder joint as it’ll pass the regular test but have impact on the long term reliability of the product. A new pin pull test method with solder ball attached and positioning the test board at an angle of 30º is employed to study the strength of pad cratering. This new method clearly reveals the failure mechanism. And a proper way to interpret the finite element analysis (FEA) result is discussed. Impact of pad dimension, width and angle of copper trace on the strength is included. Some findings not included in previous research could help to guide the design for better performance
Technical Library | 2013-01-17 15:37:21.0
A problem exists with electroless nickel / immersion gold (ENIG) surface finish on some pads, on some boards, that causes the solder joint to separate from the nickel surface, causing an open. The solder has wet and dissolved the gold. A weak tin to nickel intermetallic bond initially occurs, but the intermetallic bond cracks and separates when put under stress. Since the electroless nickel / immersion gold finish performs satisfactory in most applications, there had to be some area within the current chemistry process window that was satisfactory. The problem has been described as a 'BGA Black Pad Problem' or by HP as an 'Interfacial Fracture of BGA Packages…'[1]. A 24 variable experiment using three different chemistries was conducted during the ITRI (Interconnect Technology Research Institute) ENIG Project, Round 1, to investigate what process parameters of the chemical matrix were potentially satisfactory to use and which process parameters of the chemical matrix need to be avoided. The ITRI ENIG Project has completed Round 1 of testing and is now in the process of Round 2 TV (Test Vehicle) build.
SMTnet Express, October 28, 2021, Subscribers: 26,544, Companies: 11,461, Users: 26,907 Cracks: The Hidden Defect Cracks in ceramic chip capacitors can be introduced at any process step during surface mount assembly. Thermal shock
Surface Mount Technology Association (SMTA) | https://www.smta.org/knowledge/proceedings_abstract.cfm?PROC_ID=4996
-Nürnberg Date Published : 9/17/2017 Conference : SMTA International Abstract: This investigation focuses on the influence of voids on the reliability of solder joints for high-power LED applications
Heller 公司 | http://hellerindustries.com.cn/Vacuum-Void-Reduction-Reflow.pdf
. The root cause of voids in solder joints is understood and has been documented in numerous publications on the topic [1-3]. There are industry guidelines for characterizing voiding [4, 5
COT specializes in high quality SMT nozzles and consumables for pick and place machines. We provide special engineering design service of custom nozzles for those unique and odd components.