Electronics Forum | Mon Apr 19 20:49:13 EDT 1999 | Dave F
| Netters, | | When I reflow a PCB there is a discoloration of silkscreen and mask. It appears if Profile is too hot! But I dont think so, maybe I'm wrong? | | 1. Kester 293 no clean | 2. 2.1 C/s for 30s to 150 C | 3. .5 - .7 C/s for 60s to 185
Electronics Forum | Wed Dec 19 15:43:23 EST 2007 | cdsullivan
Hi, I was just wondering what the most common process is for silkscreen/legend removal and/or rework? Scenario: Fab house had a registration issue on some SOT-323 packages where the silkscreen encroached or was actually printed on the surface pads
Electronics Forum | Tue Apr 13 18:39:24 EDT 1999 | Tom B
| | Netters, | | | | When I reflow a PCB there is a discoloration of silkscreen and mask. It appears if Profile is too hot! But I dont think so, maybe I'm wrong? | | | | 1. Kester 293 no clean | | 2. 2.1 C/s for 30s to 150 C | | 3. .5 - .7 C/s f
Electronics Forum | Tue Apr 13 23:08:56 EDT 1999 | Jeff Sanchez
| | | Netters, | | | | | | When I reflow a PCB there is a discoloration of silkscreen and mask. It appears if Profile is too hot! But I dont think so, maybe I'm wrong? | | | | | | 1. Kester 293 no clean | | | 2. 2.1 C/s for 30s to 150 C | | | 3.
Electronics Forum | Thu Jan 28 16:29:03 EST 1999 | Tom B
Okay, Another question, if the soldermask in not cured, then it is washed will water ingress (from wash or ambient ) play havoc with capacitance or dielectric of PCB. I mean will my crystal and clock circuits start "Y2K'n" on me. OR will my PCB go
Electronics Forum | Wed Apr 21 00:35:31 EDT 1999 | Scott Cook
| Netters, | | When I reflow a PCB there is a discoloration of silkscreen and mask. It appears if Profile is too hot! But I dont think so, maybe I'm wrong? | | 1. Kester 293 no clean | 2. 2.1 C/s for 30s to 150 C | 3. .5 - .7 C/s for 60s to 185
Electronics Forum | Fri Apr 26 09:32:22 EDT 2002 | blnorman
We conformally coat over NC solder paste. No problems. We're using a platinum catalyzed addition cure silicone. The only concern with this conformal coating is cure inhibition. You must test the coating over the residues to be sure there is no in
Electronics Forum | Fri Dec 18 09:07:24 EST 2009 | tommyg_fla
dave, where I work they are having the same problems with 1B31 acrylic. The coating thickness is 6-8 mils dried so that have to do several passes with an air dry between them and a final oven cure. They think that it might be related to the heating r
Electronics Forum | Thu Jan 28 15:43:16 EST 1999 | Dave F
| Hello Netters, | | I need some info, Earl or Dave, I have a PCB that exhibits a white layer on solder side. It does not appear to be surface residues (IPA has no effect), but looks like its under solder mask. My first guess is that the LPI solde
Electronics Forum | Thu Jan 28 15:53:12 EST 1999 | Dave F
| | Hello Netters, | | | | I need some info, Earl or Dave, I have a PCB that exhibits a white layer on solder side. It does not appear to be surface residues (IPA has no effect), but looks like its under solder mask. My first guess is that the LPI