Industry News | 2012-03-09 19:28:38.0
LOS ANGELES, CA – March 9, 2012 – Qual-Pro Corporation, an industry leading electronics manufacturing service provider for high-reliability, mission-critical electronics, today announced that the company has installed conformal coating equipment. A dedicated engineering team with decades of electronics manufacturing experience supports the conformal coating function.
Technical Library | 2015-03-26 19:16:03.0
Nickel-palladium-gold-finished terminals are susceptible to creep corrosion. Excessive creep corrosion can result in device failure due to insulation resistance loss between adjacent terminals. The mixed flowing gas test has been demonstrated to produce creep corrosion on parts with nickel-palladium-gold finished terminals. Conformal coats are often used to protect printed wiring assemblies from failure due to moisture and corrosion. However, coating may not be sufficient to protect lead terminations from failure.In this study, acrylic, silicone, urethane, parylene, and atomic layer deposit (ALD) coatings were examined for their effectiveness at preventing corrosion of nickel-palladium-gold-finished terminals.
Industry News | 2016-03-03 08:27:28.0
Nordson MARCH has recently released a white paper showing the results of RF plasma processing on conformal coating adhesion, the conformity of the coating coverage, and the resulting effects on electrical functionality of a fully assembled printed circuit board. The research was done in conjunction with Nordson ASYMTEK, AirBorn Electronics, and SMART Microsystems (formerly known as Desich SMART Center). The paper can be downloaded at http://bit.ly/MARCH-PlasmaWP.
Technical Library | 2017-06-01 17:12:08.0
The corrosion of Nickel-Palladium-Gold (Ni-Pd-Au) finish terminals in humid environments is known to be reduced with the application of a conformal coating such as acrylic. Corrosion has a higher rate of occurrence around the terminal ‘knee’ of a surface mount component, which may be reduced with the application of conformal coatings. Although radio frequency (RF) plasma processing is generally known to enhance conformity of conformal coating to surfaces through ionic bombardment, the effect on the functionality of assembled printed circuit boards (PCB) is not as well known. The purpose of this study is to assess whether RF plasma processing can enhance the adhesive and coverage qualities of an acrylic conformal coating on PCBs, specifically on Ni-Pd-Au terminals with a knee, and if plasma processing has an effect on the electrical functionality of components and fully assembled PCB.
Technical Library | 2021-10-06 17:54:32.0
The corrosion of Nickel-Palladium-Gold (Ni-Pd-Au) finish terminals in humid environments is known to be reduced with the application of a conformal coating such as acrylic. Corrosion has a higher rate of occurrence around the terminal 'knee' of a surface mount component, which may be reduced with the application of conformal coatings. Although radio frequency (RF) plasma processing is generally known to enhance conformity of conformal coating to surfaces through ionic bombardment, the effect on the functionality of assembled printed circuit boards (PCB) is not as well known. The purpose of this study is to assess whether RF plasma processing can enhance the adhesive and coverage qualities of an acrylic conformal coating on PCBs
Industry News | 2012-02-10 15:56:15.0
The new Polyonics double-coated tapes are ideal for bonding materials that will be exposed to extremly high temperatures and harsh manufacturing environments. They include liners that are designed to be die cut and, due to their additional stiffness compared to transfer adhesives, can be easily auto-applied.
Electronics Forum | Tue Jun 02 14:32:58 EDT 1998 | Chris Fontaine
We have experienced poor adhesion of acrylic conformal coating to plastic bodied IC�s. The observed symptoms of this are a blistering or lifting of the coating at the surface of the component, although peel testing has revealed that this is not alwa
Electronics Forum | Tue Jun 02 18:01:47 EDT 1998 | Earl Moon
| | | We have experienced poor adhesion of acrylic conformal coating to plastic bodied IC�s. The observed symptoms of this are a blistering or lifting of the coating at the surface of the component, although peel testing has revealed that this is no
Electronics Forum | Tue Jun 02 17:36:43 EDT 1998 | Chris Fontaine
| | We have experienced poor adhesion of acrylic conformal coating to plastic bodied IC�s. The observed symptoms of this are a blistering or lifting of the coating at the surface of the component, although peel testing has revealed that this is not
Electronics Forum | Tue Jun 02 15:53:32 EDT 1998 | Earl Moon
| We have experienced poor adhesion of acrylic conformal coating to plastic bodied IC�s. The observed symptoms of this are a blistering or lifting of the coating at the surface of the component, although peel testing has revealed that this is not al