Electronics Forum | Thu Dec 12 09:35:45 EST 2002 | Randy Villeneuve
We are using Immersion tin in production. We specify Omikron-plus tin which according to the information is much better in solderability and shelf life than standard immersion tin. I am not having any problems with the finish and we are running it th
Electronics Forum | Fri Mar 18 14:22:37 EDT 2011 | bradbriggs
We recently ran into a situation where a SMT header with tin plated tails would not wet properly during reflow. Someone told us that tin plating has a shelf life and needs to be re-tinned after a length of time. I have not heard of that before. Do
Electronics Forum | Tue May 02 14:27:43 EDT 2006 | bhall
In the past we have used immersion tin as an alternative for HASL. Our biggest problem was shelf life. The tin oxidized very rapidly. We switched to immersion gold and have had great success.
Electronics Forum | Mon Feb 05 07:02:11 EST 2007 | CL
ASIR, Findings for us so far: OSP- has worked well for us for single sided boards only. We have seen problems with using it on double sided reflow applications. Also, some customers have specified OSP, but are intolerant of exposed copper. Limited
Electronics Forum | Wed Jan 04 03:08:12 EST 2023 | msirifat
Hello Stephen, thanks for the advice. We are producing LED TVs & we have a facility for SMT and manual insertion. We are also thinking of changing the board finish from OSP (due to its shorter shelf life) to ENIG/Immersion Tin.
Electronics Forum | Fri Jul 18 10:46:43 EDT 2003 | davef
If you are saying that you have discolored white tin at in-bound inspection, you have bad boards. The boards are fabricated incorrectly. Your fabricator is deficient. That is the GREAT thing about imm coatings. You can look at them and determine
Electronics Forum | Tue Jan 04 15:38:19 EST 2000 | Pat Pepper
Hi everyone: Our company is trying out immersion white tin for fine pitch assembly with what I would call mixed results. Reflow solder looks very good, but wave solder looks somewhat grainy (this may not be a problem in actuality). We had dewettin
Electronics Forum | Tue Aug 09 11:57:11 EDT 2005 | Board House
Hi Ted, I am a Sales Manager for a Circuit board Manufacture in MN. We have seen the Majority of our Customer base switch to Enig do to shelf life issues of silver and Tin. Silver, Tin & OSP all have a shelf life between 6 - 8 Mos. Enig is betwee
Electronics Forum | Thu Aug 29 07:21:28 EDT 2002 | nifhail
What are other testing/process step that we should do if we where to use the old date code QFPs other than solderability and baking ? What is the plating composition normally %? lead, % tin etc. I have my policy not to accept the more than 12 mont
Electronics Forum | Fri Feb 28 01:36:43 EST 2020 | crystal12
> What is the use of gold plated boards? <BR> <BR> With the increasing integration of IC, the more IC the more dense. The vertical tin spray process is difficult to flatten the pads, which brings difficulty to the SMT mounting, and