Electronics Forum | Fri May 13 14:08:39 EDT 2011 | eezday
This appears to be black-pad and is often the result of using specs that call for gold plating that is too thick. The black pad is corrosion that is created between the gold and electroless nickel during the gold plating process. This is counter in
Electronics Forum | Thu Jul 02 15:23:15 EDT 1998 | Justin Medernach
| | I'm having a problem getting good reflow on gold sufaced boards. The profile looks good and I have adjusted it both hotter and colder and adjusted the various times ( soak, reflow ) to no avail. What realy gets me Is that a month ago we built som
Electronics Forum | Fri Mar 17 07:51:49 EST 2000 | Peter Barton
John, I have had previous experience of immersion silver coated PCB's in place of HASL coated type using no-clean processing with little or no problem at all. All of the process parameters were left unchanged. There is a very minor difference in th
Electronics Forum | Thu Jun 15 12:57:12 EDT 2000 | Dave F
0.0006" LT Total pad height = Thickness of ( Copper pad + OSP ) = 0.0014" + 0.00000157" = ~0.0014" (You must be using an organic solderability preservative (OSP) or Electroless Nickel immersion gold (ENIG) because 0.003" tin/lead or white tin would
Electronics Forum | Fri Mar 17 07:51:49 EST 2000 | Peter Barton
John, I have had previous experience of immersion silver coated PCB's in place of HASL coated type using no-clean processing with little or no problem at all. All of the process parameters were left unchanged. There is a very minor difference in th
Electronics Forum | Fri Feb 09 20:05:15 EST 2001 | benefid
The ENIG process will yield between 3-7 micro inches (110 - 275 microns) of gold over the nickel barrier. This thickness range is pretty much the limit as this is a self limiting displacement reaction process. Once all surface nickel ions are repl
Electronics Forum | Tue Apr 17 10:17:10 EDT 2001 | genny
Hi, ENIG finish is the same reason I came to this forum for the first time a few months ago. I found a bunch of useful information by searching the archives. Check it out. ENIG has some good properties like flatness, and the process control has i
Electronics Forum | Thu Oct 21 14:02:32 EDT 1999 | Ron Costa
We are a contract manufacturer currently building a job with IBM CBGA-255 devices and 20mil QFP's that are close to each other. We use a 6 mil laser cut and electro polished stencil with one to one apertures on the BGA's. The customer is experiencing
Electronics Forum | Wed Aug 18 12:35:41 EDT 1999 | Earl Moon
| | WE ARE CURRENTLY HAVING PROBLEMS REFLOWING BOARDS WITH WHITE TIN PLATING. WE ARE NOT GETTING GOOD WETTING ON THE PADS. | | WE HAVE CHECKED THE REFLOW PROFILE AND TRIED DIFFERENT PASTE'S. | | WE THINK THERE MAY BE CONTAMINATION OR OXIDATION ON THE
Electronics Forum | Thu Jul 15 18:58:48 EDT 1999 | Earl Moon
| We are currently assemblying several different board type with gold plated lands with varying results. Can any of you that has successful experience in this area give me some pointers. What paste do you use? Do you use the recommended reflow pro