Electronics Forum | Fri Sep 21 10:35:37 EDT 2012 | davef
Flash gold is just thin electrolytic gold plating over electroless nickel or electrolytic nickel. Flash gold plating ... * Less than 3 microinch thick will be porous and take solder poorly * Greater than 10 microinch thick will cause brittle solder c
Electronics Forum | Fri Apr 29 14:16:16 EDT 2011 | ppcbs
Below is the long explanation. This defect is most commonly found with BGA components, but can arrise with all components. I see it happening more now with lead free boards that are being assembled with a no clean flux. Best short term remedy is t
Electronics Forum | Mon Aug 10 21:52:34 EDT 1998 | Dave F
| | | Is there any problem using SMT on gold boards? 15 years ago we were told not to use gold boards, but I can't remember why. Judging by the other postings it now appears to be common. Only problem I see is that the nickel should be plated, not
Electronics Forum | Tue Aug 11 07:51:57 EDT 1998 | Earl Moon
| | | | Is there any problem using SMT on gold boards? 15 years ago we were told not to use gold boards, but I can't remember why. Judging by the other postings it now appears to be common. Only problem I see is that the nickel should be plated, n
Electronics Forum | Thu Aug 06 17:25:55 EDT 1998 | Earl Moon
| Is there any problem using SMT on gold boards? 15 years ago we were told not to use gold boards, but I can't remember why. Judging by the other postings it now appears to be common. Only problem I see is that the nickel should be plated, not ele
Electronics Forum | Tue Apr 17 08:29:12 EDT 2001 | Geertjan de Beijer
My name is Geertjan de Beijer and I am new on this forum. I have a question about Electroless Nickel/Gold finishes. Until now we always use a HAL finish on our PCB's. Since we are using compontents with pitches of 0.5mm we notice that the HAL finis
Electronics Forum | Fri Jun 19 13:40:25 EDT 1998 | Terry Burnette
| Has anyone had experience with placing BGA on gold plated boards. I thought I read a while ago there was a problem with embrittlment causing cracked joints. If anyone has experience with this your feedback would be great. | Mike There has been a
Electronics Forum | Thu Aug 25 17:24:44 EDT 2016 | davef
Gold should not be corroding in salt water. I have swum hundreds of miles in salt water with my wedding ring on my finger. My ring is a shiny and corrosion-free as the day it was cast over 120 years ago. It's possible that your gold thickness of 0.0
Electronics Forum | Wed Apr 21 15:28:02 EDT 2004 | markhoch
I have a new customer who is recommending a Sulfamate Nickel Finish for his boards. I'm not really familiar with this process. Is anybody else? How does it differ from electroless nickel? Can a standard NC solder paste cut the mustard with this stuff
Electronics Forum | Tue Feb 01 06:54:19 EST 2000 | Roni H.
Hi, Does anyone have experience with gold over nickel (electroless) PCB finish: - Repeatble quality from PCB mfg. (very "painfull" with ENTEK). - Environment condition sensitivity. - Thermal processes sensitivity. - Solderability (Reflow & wave). -