Electronics Forum | Thu Aug 05 11:51:44 EDT 1999 | Wolfgang Busko
| | | | | | | | | | | | Hello, | | | If you are using no-clean and they are entrapped in the flux it is also IPC accepted but i havent found a customer yet who agrees with that. Im sure you have checked your profile. I had the same problem with chi
Electronics Forum | Mon Jan 05 16:07:21 EST 1998 | Terry Burnette
| | Hello all, | | I have experienced broken ceramic SMT parts. Most of the time, | | we have found fractured inductive beads. Once in awhile, we find | | broken Ceramic Caps. All parts we use are 1206 form factors and | | we use tape and reel...
Electronics Forum | Fri Mar 17 16:58:52 EST 2006 | mikecollier
We are currently struggling with a particularly difficult component selection form our designers. This is a custom BGA, 592 balls, metal cover with a very large bead of adhesive using to retain the cover. We have had significant fallout (greater th
Electronics Forum | Sat Aug 07 11:47:47 EDT 1999 | JohnW
| | | | | | | | | | | | Hello, | | | If you are using no-clean and they are entrapped in the flux it is also IPC accepted but i havent found a customer yet who agrees with that. Im sure you have checked your profile. I had the same problem with chi
Electronics Forum | Thu Aug 05 12:20:06 EDT 1999 | John Thorup
| | | | | | | | | | | | | | | Hello, | | | | If you are using no-clean and they are entrapped in the flux it is also IPC accepted but i havent found a customer yet who agrees with that. Im sure you have checked your profile. I had the same problem
Electronics Forum | Fri Aug 06 06:13:37 EDT 1999 | Wolfgang Busko
| | | | | | | | | | | | | | | | | | Hello, | | | | | If you are using no-clean and they are entrapped in the flux it is also IPC accepted but i havent found a customer yet who agrees with that. Im sure you have checked your profile. I had the same
Electronics Forum | Mon Jun 08 14:52:16 EDT 1998 | Gary Simbulan
| Earl, et al, | Boy things get old and cold around here fast. I promised more detail on my capactior problem and I thought I could drop something completely different in the same message and tell a tale of solder balls. | First the caps. We stil