Electronics Forum | Thu Sep 30 16:28:51 EDT 2010 | 18424
Hello All, looking for some help from you guru's. I have several Enig boards with solderability problems. Components ranging from 0402's to ssop's. Using AIM W/S leaded solder paste, profile is beautiful and has been for years running the same produc
Electronics Forum | Mon Sep 11 04:10:46 EDT 2000 | Jim Arnold
I spent 25 years operating my own hybrid shop working with surface mount components, soldering materials and procedures. Dealing all the while with it's associated surprises and problems such as yours. Now-a-days I get paid to investigate and attemp
Electronics Forum | Sun May 16 10:11:50 EDT 1999 | M Cox
| I'm running memory module product- SMT double reflow ( 12 modules per panel). I'm using the epoxy base solder paste in order to reduce the flux spattering problem onto the gold finger which could lead to the intermittent contact problem. | | I do
Electronics Forum | Wed Jul 14 11:36:56 EDT 1999 | Jimmy Strain
| | | Hi All, | | | Does any one experienced the solder on gold finger after | | | reflow. Its about 5 to 8 mils diameter . | | | We'd clean the entire screen printer, mounter & reflow as well, | | | but doesn't help much. | | | | | | | | Mr Kong..
Electronics Forum | Wed Aug 12 07:22:52 EDT 1998 | Earl Moon
| | | | | Is there any problem using SMT on gold boards? 15 years ago we were told not to use gold boards, but I can't remember why. Judging by the other postings it now appears to be common. Only problem I see is that the nickel should be plated,
Career Center | Shen Zhen, China | Management,Sales/Marketing
Working in GLORYPCB for 10 years.knowing electronic supply chain very well. especially for PCB PCBA assembly and other Electronic Manufacturing Service.Glorypcb is a professional electronic manufacturer located in Shenzhen with three facilities.offe
Electronics Forum | Wed Jun 18 03:51:04 EDT 2008 | bing007
We have evaluated vapour phase in the past and was very impressed on how simple and easy it was to use and control. Gods send when being pushed in an audit because so little can be changed and will work within the chemistry within the unit. I so want
Electronics Forum | Mon Sep 27 08:52:11 EDT 1999 | Brian
| i had a problem here, during the wave soldering process, we apply a water soluble mask on the gold finger to protect it from contamination. But after washing, there is still some mask left on the gold finger. | Can anyone pls advise is there any pa
Electronics Forum | Fri May 28 16:30:39 EDT 1999 | JohnW
| Yes l know this problem keeps cropping up on the forum but l've missed some of the follow-ups. | | Our problem is that the lifting only occurs on 3% of production so actually detecting an improvement is difficult. We're actually having to inspect
Electronics Forum | Fri Aug 29 09:39:08 EDT 2014 | rgduval
I'll try to deal with the issues as you've presented them. 1. Blistering/delamination, shown in photo 2. The most likely cause of blistering/delamination like this is moisture in the boards. The moisture can get into the boards in multiple ways..