Electronics Forum | Tue Jun 03 01:03:04 EDT 2008 | daxman
Hi, I think what you are describing is a half-etch QFN, which causes the 3 mil gap. In our process, we don't require solder to bridge this gap as it's internally connected to the bottom lead. I'm not sure if this is the question you're asking, but
Electronics Forum | Sun Oct 28 23:32:25 EST 2001 | flynhi34
Thanks for the info on the printers. I have printed conductive epoxy on Dek 265 with great success in the past. The issue I have is that I need to attach with both epoxy and solder on the same side of the PCB. I could double print. Print conductiv
Electronics Forum | Tue Jan 04 09:26:22 EST 2011 | scottp
We've been doing this for over 10 years using flux. We print a tacky flux first using an 0.002 or 0.003" thick stencil, then print paste using a thicker stencil with the underside half etched to keep it away from the flux. In our case, we can't jus
Electronics Forum | Mon Nov 12 16:14:47 EST 2001 | davef
Yes!!! How can we assemble boards with 20 pitch when we allow 0.008� error to the master art? Excellent question!!! IPC-D-300G has nothing to do with assembler requirements. It is written by and for fabricators, so that they can be comfortable.
Electronics Forum | Mon Jul 13 07:25:09 EDT 2009 | hcarrasco
Hi everybody, > We recently start to use an ultrasonic stencil cleaners for our stencils. > It' work well, but after some time, we saw a lot of fiducial that the black > epoxy have been partially or totaly remove. I want to know if someone h
Electronics Forum | Tue Jan 03 17:38:38 EST 2012 | davef
Here's two ideas fro the fine SMTnet Archives: * On the bare board, during design / layout, the basic shape of the jumper is a 125 thou disc of copper [that of course is eventually covered with whatever solderability preservative we use on the board]
Electronics Forum | Wed Mar 17 21:42:19 EST 1999 | Chuck Garth
We are presently aluminum wirebonding to gold plated lands. Our board manufacturer has been very inconsistient in the quality. It seems as though theey are over etched by about half the amount they should be. Can anyone give me the spec's that normal
Electronics Forum | Tue Nov 27 10:16:07 EST 2001 | davef
Oooo, I get it. We do that trick on the wave solder side of boards. On the bare board, during design / layout, the basic shape of the jumper is a 125 thou disc of copper [that of course is eventually covered with whatever solderability preservative
Electronics Forum | Thu Apr 15 14:56:43 EDT 1999 | Dave F
| Can anyone suggest or identifiy standards which tabulate the following: | | Conductor width, cross sectional and area conductor thickness for PCB's carrying up to 70 Amps? | Barry: Check: 1 Printed Circuits Handbook (Clyde F. Coombs) 2 Microel
Electronics Forum | Tue Apr 27 05:26:14 EDT 1999 | Charles Stringer
| | Hey MoonMan, | | | | Did I catch in one of your fabulous threads that you're using Tetra stencils? I'm anxious to find out how you're liking them. | | | | We we're all set up to go to Tetras, then mgt decided to close down our factory - Dooop!