Electronics Forum | Tue Mar 15 10:44:42 EST 2005 | jdengler
-If the aperture volume is the same, there will be more solder on the HASL finish joint due to the solder already present on the pad. This difference is not usually enough to cause insufficiant solder volume but will "look different". Sometimes an
Electronics Forum | Thu Jan 15 08:39:26 EST 2004 | Patrick
Thanks for the reply, I do know that the HASL finish is "domed " on opposite sides of a QFP site & "smooth" on the other two sides. (ie. Sides 1 & 3 are domed, & sides 2 & 4 are smooth ) depending on the direction the PCB was extracted from sol
Electronics Forum | Fri Sep 24 09:49:53 EDT 1999 | C.K.
Hi Folks: We've been having bridging problems on our fine-pitch QFP's, despite thorough inspection of paste height, volume, and placement accuracies....profiles look good also. The bridging is happening after coming out of reflow...one last thing t
Electronics Forum | Fri Jul 23 06:48:23 EDT 2004 | mattkehoe
I am actually getting opinions that point to contaminated copper under the HASL finish. We've seen some "fish eyes" where the HASL is pulled away from the copper exposing a pin hole of copper that can be seen through the HASL finsh. We are planning o
Electronics Forum | Wed Jan 26 17:36:22 EST 2011 | ck_the_flip
had a quick question regarding compatibility of Sn100C HASL finish and regular Sn63 solder paste. Does the thermal profile have to reach Sn100C eutectic temps. in order for the Sn 100C HASL to coaelesce with the Sn63 Solder paste? How reliable is t
Electronics Forum | Thu Aug 27 02:55:11 EDT 2009 | smtirl
Alloy is Sn/Pb on a HASL finish. Standard no-clean flux reflowed in Nitrogen.
Electronics Forum | Tue Jul 06 11:58:44 EDT 2010 | baildl632
What type of finish are the PCB's? HASL, tin immersion, silver immersion,........we've seen all the above problems with HASL finished boards. Usually either reheating w/ a soldering iron or "burnishing" with a scotch brite pad has worked for us.
Electronics Forum | Tue Sep 14 10:10:39 EDT 2010 | teamcanada
We are having an issue with a PCB supplier. Their Tin HASL layer seems to be the problem. We have triedworking with them to correct their process. What seems to have helped is lowering their temperature of the Tin dip from 540 F to 510 F.We still ha
Electronics Forum | Tue Jul 27 07:18:44 EDT 2004 | Nippy
How does the HASL finish and stencil match ? I have seen ocasions on fine pitch devices where the HASL can protrude into the stencil aperture either pulling paste down on the snap off or completely blocking the aperture and getting no paste.
Electronics Forum | Thu Jul 05 11:14:04 EDT 2001 | caldon
We can offer two ways. We have a process control tool for OSP boards to validate the finish......but the dates yer talking may be best to take Daves F suggestion. NOW as far as the HASL finish goes...We may have your answer. We can Chemically revers