Electronics Forum | Tue Sep 21 09:33:30 EDT 1999 | Scott Davies
| | | My stencil thickness is 6 mil and we got qfp's with fine pitch. | | | how many percent should i reduce my stencil aperture using a 6 mil stencil for 0.5 mm pitch and 0.4 mm pitch ? | | | | | | thanks | | | | | We use 6 mil lasercut stencils w
Electronics Forum | Tue Sep 21 17:24:58 EDT 1999 | John Thorup
| | | | My stencil thickness is 6 mil and we got qfp's with fine pitch. | | | | how many percent should i reduce my stencil aperture using a 6 mil stencil for 0.5 mm pitch and 0.4 mm pitch ? | | | | | | | | thanks | | | | | | | We use 6 mil lasercu
Electronics Forum | Thu Mar 29 15:29:11 EST 2001 | johnw
measuring Paste volume or at least paste height is an essencial part of any SMT process. You've got to control those input's.... Paste volume determines how much solder is available for your joint so theres a direct to joint reliability / PCB reliabi
Electronics Forum | Tue Dec 08 15:19:42 EST 2015 | proceng1
Apply the correct amount of paste for the pad size should work ok, as long as the part starts out in the paste. If you have a reduced aperture and the leg doesn't quite touch any paste could result in non-wetting or insufficient solder issues. I gu
Electronics Forum | Thu Mar 13 14:12:31 EDT 2014 | davef
You're creating a new alloy on the surface of your board. The alloy will have a melting point determined by the constituent metals of the alloy. Your alloy consists of: * Lead-free HASL solderability protection on the board * Lead-free solder paste *
Electronics Forum | Wed Sep 22 21:12:16 EDT 1999 | se
| | | | My stencil thickness is 6 mil and we got qfp's with fine pitch. | | | | how many percent should i reduce my stencil aperture using a 6 mil stencil for 0.5 mm pitch and 0.4 mm pitch ? | | | | | | | | thanks | | | | | | | We use 6 mil lasercu
Electronics Forum | Wed Jan 19 08:40:53 EST 2000 | Wolfgang Busko
Hi Erico, I think it�s just a naming problem. Under the topic of tombstone there are a lot of causes for different appearances of this symptom. Shouldn�t be always the errected position that occurs. In your case it seems that either the components so
Electronics Forum | Fri Apr 30 11:03:27 EDT 1999 | Wade Oberle
| | Ok folk's has anyone used Alpha Metal's UP78 solder paste ? | | | | Our place is looking to move to that as the way to go, getting rid of the Hereaus 362's and Alpha 737's of the current set up. | | | | My question's are really : | | how is the
Electronics Forum | Wed Mar 21 16:32:03 EST 2001 | mparker
The root cause is dependant on the type of solder "splash", ball, whatever, that you are seeing post reflow. If it is smears, then cleaning the stencil underside is probably the answer. Are you using automatic wipers? How many print cycles between w
Electronics Forum | Mon Jul 05 03:53:36 EDT 2004 | johnwnz
Hey, this is something that I've looked at and published a paper on back in 2003 at Apex, actually pert of one, the other part was lookign at how effective X-ray systems (lamanography systems) were at detecting & measuring BGA void size accuratly (co