Electronics Forum | Fri May 18 06:49:58 EDT 2012 | kahrpr
We us a lot of 1B31 it could be one of the most common coatings out there. We do not clean the boards and do not have an issue. I would check the solder mask compatibly. I would also see how the 3rd party company is testing the boards what criteria o
Electronics Forum | Wed Mar 04 10:05:13 EST 2020 | dontfeedphils
In a past life I used a Swam Blaster from Crystal Mark with the media from them as well. I used it on Humiseal 1A31 and 1B31 (I think those were the products, it's been a little while). This machine and material were awesome IMO. Made CC removal a
Electronics Forum | Wed Apr 18 09:16:51 EDT 2007 | Cecil
We currently have an assembly that we have to mask the surface of several (24)SMT components where thermal compound is applied at a latter operation. These component packages vary from BGA's to QFP's. After the thermal compound is applied the PWA is
Electronics Forum | Thu Sep 06 15:36:27 EDT 2007 | kpm135
My company recently aquired an asymtek coating machine and I have been using Humiseal 1B31, an acrylic coating, in it to coat all the boards given to me. They have now come to me and asked if it is possible to run Humiseal 1A33, a urethane coating, t
Electronics Forum | Mon Dec 28 09:12:56 EST 2009 | kpm135
@tommyg_fla According to the TDS the recommended coating thickness for Humiseal 1B31 is only 1-3 mils so if I had to guess I would say your issue might be that you're re-coating over the first pass too soon. All the solvent hasn't evaporated and the
Electronics Forum | Wed Nov 09 09:27:44 EST 2011 | edmaya33
If you are using a Humiseal. try UV-40 gel which is about 20Kcps. it will dam your material from capillary flow. It should be applied prior to coating of your low viscous material.
Electronics Forum | Tue Nov 26 18:41:14 EST 2013 | triciawmcgough
Dear Mike, I've forwarded your question to the experts at Nordson ASYMTEK. I believe most of the team are on leave for the holidays, but hopefully we'll have an answer for you next week. Thanks!
Electronics Forum | Thu Dec 05 02:22:29 EST 2013 | mg2013
Hi Tricia, thanks a lot for your help, i will contact Nordson Asymtek immediately! Greetings Michael
Electronics Forum | Wed Jul 20 10:07:05 EDT 2005 | cecil
Does anyone have any input on the need to bake out an assembly prior to the conformal coat process? I understand baking out components/pwb's prior to processing through the reflow or wave solder process if the material shows excess moisture absorbtio
Electronics Forum | Wed Jan 31 10:56:23 EST 2018 | dontfeedphils
I'm working on bringing up a new conformal coat process/workcenter and have a few questions I'm hoping someone might have experience with. Right now we're manually spraying both coating materials (1B31 and 1A33 from Humiseal) using HVLP guns. I run