Electronics Forum | Thu Jan 22 09:04:22 EST 2009 | mefloump
Humiseal recommends a 1 to 1 mix ratio of 1B31 and Thinner 521. I have for that I need to thin my ratio more to get humiseal to spray correctly in our PVA650. Also I am using Humiseal 1B73 but the tech data sheets say the same for spraying. Try thinn
Electronics Forum | Wed Feb 28 20:10:08 EST 2001 | mhunter
Checked the archives with no luck. Anyone have a reliable test method of verifying acrylic conformal coat cure. Using Humiseal 1B31 mixed with approximately 30% solvent, spraying with a Nordson. Thanks in advance.
Electronics Forum | Wed Feb 28 20:16:26 EST 2001 | mhunter
Checked the archives with no luck. Anyone have a reliable test method of verifying acrylic conformal coat cure. Using Humiseal 1B31 mixed with approximately 30% solvent, spraying with a Nordson. Thanks in advance.
Electronics Forum | Fri Jan 16 06:53:33 EST 2009 | stevewilde
I am using Humiseal 1B31 conformal coating and xylene mix on a PVA coating machine. Bubbles are appearing between the pins of LCCs mainly and bubbling is worse when put through the IR oven. Does anyone have any suggestions or tips to elliminate this
Electronics Forum | Mon Aug 09 07:13:08 EDT 2010 | raghu
We have PVA 354Bench top conformal coating machine. We are going to procure the Humiseal 1B31 material. Is this material is suitable for this model of machine? Is there any special pecautions to be taken while programming? What are the main problemsd
Electronics Forum | Tue Aug 10 01:02:31 EDT 2010 | raghu
We have PVA 354Bench top conformal coating machine. We are going to procure the Humiseal 1B31 material. Is this material is suitable for this model of machine? Is there any special pecautions to be taken while programming? What are the main problems
Electronics Forum | Fri Nov 12 04:48:02 EST 2010 | raghu
thanks for your reply sir, for conformal coating Humiseal 1B31, what are the preferable staking materials? please suggest us..
Electronics Forum | Wed Nov 24 13:36:48 EST 2010 | diamondmt
I would suggest Zymet CN-1703 for staking of the components using this coating material we use it very extensively with Humiseal 1B31, if you would like; I would be happy to coat a couple of your samples for your evaluation.
Electronics Forum | Thu May 02 14:07:53 EDT 2013 | duso02
I would suggest lowering the viscosity even more. Humiseal even sells 1B31 pre-mixed specifically for spray machines and the highest they go is 65cps.
Electronics Forum | Thu Aug 12 13:18:43 EDT 2021 | conro
The HumiSeal 1B31 is actually pretty fast drying e.g. 24h @ room temperature or 30min @ 76 °C Link