Electronics Forum | Thu Jan 22 09:04:22 EST 2009 | mefloump
Humiseal recommends a 1 to 1 mix ratio of 1B31 and Thinner 521. I have for that I need to thin my ratio more to get humiseal to spray correctly in our PVA650. Also I am using Humiseal 1B73 but the tech data sheets say the same for spraying. Try thinn
Electronics Forum | Tue Nov 30 11:08:22 EST 2004 | jdumont
Hey all, we will be starting to coat our PCB's soon. I am looking for info on what type of UV light is needed to inspect the boards. We will be using Humiseal 1B73 Acrylic coating. TIA, JD
Electronics Forum | Fri Feb 18 11:25:14 EST 2005 | davef
It's weird that it would be just 0805. When we see this it relates to a single part number and it goes way after a time. We use a Humiseal 1B73. I've emailed you the contact for a person that is very knowledgeable on conformal coatings.
Electronics Forum | Sat Jul 09 08:18:10 EDT 2005 | jdumont
Try Ellsworth Adhesives. We have good luck with them getting 1B73 in here fast on most occasions. www.ellsworth.com ...and no I dont work for them or know anyone who does!
Electronics Forum | Mon May 24 19:37:57 EDT 2010 | jry74
I am new Engineer in conformal coating and I am looking for help with dewetting. What "Tricks of the trade" can I try to reduce or eliminate dewetting? We use a lot of Conap CE 1155 and Humiseal 1B73? Any help would be appreciated!!!
Electronics Forum | Mon Jun 25 11:55:47 EDT 2007 | ck_the_flip
I don't think THEY (Humiseal) know how their material cures. I have a data sheet from them for 1B73, and it says 24 hours at room temperature or 30 min. @ 170�F. We use our in-line oven mainly to dry the material and make it tack-free. You would
Electronics Forum | Tue Dec 02 14:31:48 EST 2008 | dontfeedphils
Hey guys, just joined the site and I'm looking for some help. In our coating department we are running a Asymtek C-740 with a Jet and film coater. The coating that we are using is Humiseal 1B73 acrylic. The problem that we are having is that the C
Electronics Forum | Mon Jun 25 12:23:15 EDT 2007 | davef
Once the HumiSeal conformal coating has been applied to the printed circuit board it is usually best to allow the material to reach a touch-dry stage, before heating the board to accelerate the cure schedule. This avoids potential problems such as bu
Electronics Forum | Thu Nov 23 23:59:25 EST 2000 | terry sun
Hello to all out there, We're considering CC process,and would like to know some defferences between SSC3 of Electrolube and Humiseal 1B73, yes,I know that SSC3 is silicone one,and Humiseal 1B73 is solvent based acrylic as well as other basic propert
Electronics Forum | Tue Nov 28 13:21:33 EST 2000 | Graham Naisbitt
Terry The SCC3 product is a vinyl modified silicone. It is less able to perform at low temps as it becomes brittle. It is not easy to repair because it is essentially silicone. It is not a qualified material to the MIL-I-46058 Spec. Are you sure yo