Electronics Forum | Thu May 09 17:13:10 EDT 2002 | davef
We are converting all our ENIG to imm silver. CHARACTERISTICS * Nominal thickness of the deposit will be 0.1 to 0.3 microns. * Deposit is flat and uniform * It will withstand multiple heat cycles in assembly, which can be problematic with tradition
Electronics Forum | Wed Jan 24 10:08:36 EST 2007 | electronhose
Immersion Silver, ImAg, is becoming the finish of preference. This is due to it having similar process limits vs. SnPb HASL. There were some early concerns about shelf life, but new chemistries have extended finish shelf life to 12 months+. Many boar
Electronics Forum | Thu Feb 21 03:25:58 EST 2008 | jlawson
I have seen smt chip varistors with Pd/Ag teminations that had poor wetting in terms of good fillet in LF (sac305) soldering. We found that the solder tended to be attracted to the plating on the part and off the actual pad (silver Immersion). This c
Electronics Forum | Mon Feb 28 04:10:07 EST 2005 | Rob
Hi Dave, Was planning on skipping the paste step & screen printing the adhesive straight onto the pad, then placing the component into the glue & curing. (Board has LEDs only) Regarding the lead-free HASL issue - not entirely sure on the board man
Electronics Forum | Thu Aug 31 18:59:55 EDT 2000 | Brian W.
Our customers use OSP, HASL, immersion tin and immersion gold as board finishes. If I recommend a finish to the customer, it is one of the immersion finishes or OSP. Those finishes have the advantage of a flat surface to deposit paste. HASL has va
Electronics Forum | Mon Jul 05 03:44:53 EDT 2004 | johnwnz
Dave, I'm going to disagree with you on the ENIG, it's my 3rd choice only just beating out OSP for that 4th spot. 1. Immersion Silver - cheaper than ENIG, as flat and no issues with Brittle interface (black pad) or Gold Embrittlement) Longer shelf l
Electronics Forum | Tue Aug 24 21:52:06 EDT 2004 | rose
recently I met one very interesting issue with my board and connector. substrate of the board is copper with immersion silver, pad size is about 3x1mm. we print lead-free paste on the pad, then put the connector on the paste. The board was reflowed u
Electronics Forum | Wed Aug 25 20:48:17 EDT 2004 | rose
Hello recently I met one very interesting issue with my board and connector. substrate of the board is copper with immersion silver, pad size is about 3x1mm. we print lead-free paste on the pad, then put the connector on the paste. The board was refl
Electronics Forum | Tue Sep 14 14:07:45 EDT 2010 | grahamcooper22
Hi Gani, HASL is normally very good for solderability providing there is a good consistent coating of HASL on the pcb pad. But it is not unusual to have a very thin coating of HASL on the pad and this is poor for solderability. You then have tin/copp
Electronics Forum | Thu Jan 22 20:14:44 EST 2009 | herman
If you wish to specify ENIG, your best method of doing it is to simply invoke IPC-4552 (or IPC-4553 for immersion silver) on the fabrication drawing. These IPC standards define ENIG and IAg, and I believe they specify 150-180 uinches of nickel covere