Electronics Forum | Fri Jul 18 10:46:43 EDT 2003 | davef
If you are saying that you have discolored white tin at in-bound inspection, you have bad boards. The boards are fabricated incorrectly. Your fabricator is deficient. That is the GREAT thing about imm coatings. You can look at them and determine
Electronics Forum | Fri Jun 18 12:20:16 EDT 1999 | John Thorup
| Now don't everyone jump on this at once, but it seems time for me to send out copies of my not even close to being dated copy of an article about HASL. Though it was published in 1992, in Printed Circuit Fabrication Magazine, and it got rave review
Electronics Forum | Sun Jul 26 07:09:25 EDT 2015 | orbitcoms
Thank you for your prompt response. The boards we have made for us current are Immersed Gold treated because we have been hand soldering and needed flat finish that would solder ok without tarnishing too quickly. I will take a look at the link you pr
Electronics Forum | Mon Nov 19 20:15:39 EST 2001 | davef
Now, that is one thickass board!!! The rant first: If our �board supplier changed our board surface finish on� anything without our approval, the board supplier would be an �X�. Life has enough surprises. And of all the flat finishes available, h
Electronics Forum | Mon Dec 06 03:54:57 EST 1999 | Chris May
Hi Russ, I have a similar situation. I have been told that this can be caused by the nickel, over which the gold is plated, can result in suspect joints, embrittlement etc. Some joints can even be weak and broken without much force on some of my boa
Electronics Forum | Wed Jan 05 11:11:09 EST 2000 | Dave F
Hey Pat: My responses are: 1. Does anyone have experience with the shelf life on immersion white tin? If so, how long can the boards be stored without adversely affecting solderability. I've heard one year. No, we don�t, because we turn boards fa
Electronics Forum | Mon Aug 28 12:41:35 EDT 2000 | JAX
MoonMan, I'll take a crack at the list. Feel free to answer the ones I don't! 1. Solderability is a parameter which indicates how well a component can be soldered. As far as Solder Termination Coatings go, here are some up�s and down�s of a few. Ha
Electronics Forum | Mon Apr 23 17:30:08 EDT 2001 | davef
Step 1: Print paste on the board, skip placement, reflow the board, check solderability. Step 2: Goto Step 1. White Tin Solderability: The most common reason for solderability issues with the white tin surface coating during multiple thermal excur
Electronics Forum | Fri Jun 18 14:07:50 EDT 1999 | Earl Moon
| | Now don't everyone jump on this at once, but it seems time for me to send out copies of my not even close to being dated copy of an article about HASL. Though it was published in 1992, in Printed Circuit Fabrication Magazine, and it got rave revi
Electronics Forum | Wed Dec 22 01:39:06 EST 2010 | boardhouse
Hi Johan, As a Asian board supplier - I would not recommend using Lead free hasl on any product that has BGA, you would be just looking for issues, flatness being the main. I agree with one of the other replies - Your purchasing dept. should not be