Electronics Forum | Tue Feb 01 14:21:24 EST 2000 | Dennis VanBuren
We are considering the use of Immersion Silver for a PCB surface finish. We currently use Immersion Gold surface finish, which has served us well. However, recent discussions on the cracking of corner joints on large pin count BGA packages, with the
Electronics Forum | Wed Jan 24 10:08:36 EST 2007 | electronhose
Immersion Silver, ImAg, is becoming the finish of preference. This is due to it having similar process limits vs. SnPb HASL. There were some early concerns about shelf life, but new chemistries have extended finish shelf life to 12 months+. Many boar
Electronics Forum | Tue Aug 09 11:57:11 EDT 2005 | Board House
Hi Ted, I am a Sales Manager for a Circuit board Manufacture in MN. We have seen the Majority of our Customer base switch to Enig do to shelf life issues of silver and Tin. Silver, Tin & OSP all have a shelf life between 6 - 8 Mos. Enig is betwee
Electronics Forum | Mon Jul 05 03:44:53 EDT 2004 | johnwnz
Dave, I'm going to disagree with you on the ENIG, it's my 3rd choice only just beating out OSP for that 4th spot. 1. Immersion Silver - cheaper than ENIG, as flat and no issues with Brittle interface (black pad) or Gold Embrittlement) Longer shelf l
Electronics Forum | Fri Mar 17 07:51:49 EST 2000 | Peter Barton
John, I have had previous experience of immersion silver coated PCB's in place of HASL coated type using no-clean processing with little or no problem at all. All of the process parameters were left unchanged. There is a very minor difference in th
Electronics Forum | Fri Mar 17 07:51:49 EST 2000 | Peter Barton
John, I have had previous experience of immersion silver coated PCB's in place of HASL coated type using no-clean processing with little or no problem at all. All of the process parameters were left unchanged. There is a very minor difference in th
Electronics Forum | Thu Oct 07 08:13:52 EDT 2010 | remullis
I just swapped from the HASL to Immersion Silver mainly because the board house we use could not maintain consistency in keeping the pads level. I was constantly battling bumps and bad finishes on the pads. They are able to give me a consistent board
Electronics Forum | Mon May 13 11:17:57 EDT 2002 | genny
I think for our company, the reason we have not yet tried it is two fold. One - we are just barely starting to see a need on a new product under design for a flat finish, so currently we don't use any of the really flat finishes available. Two - Silv
Electronics Forum | Thu Mar 24 07:06:06 EST 2005 | davef
There's a lot of comparison tables on the web. Here's one: Properties - Summary [A Winlow Circatex] Attribute||Hasl||Immersion Silver||Immersion Tin||Electroless Pd||OSP||Eless Ni / Imm Au Shelf Life (months)||12||12||12||12||12||6 Multiple Reflows
Electronics Forum | Thu Aug 31 12:17:56 EDT 2000 | mike weekes
We are considering alternative Board Finishes to our existing HASL process. The HASL effects opens on 25 and 20 mil packages after reflow and we know if the advantages of CuOSP and other alternatives. OUR Concern: Is there a shelf life and handlin