Electronics Forum | Tue Sep 30 14:16:49 EDT 2003 | davef
While your waiting for others to respond, search to fine SMTnet Archives on: "solder and gold and finger"
Electronics Forum | Mon Nov 01 17:13:37 EST 1999 | Mark W.
Jason, What is the revision of IPC you are referring too?? IPC 610 rev. b requires 75% fill on classes 2 & 3. Class 2 does allow the exception of 50% fill if the PCB has a Metal Core or Thermal/Heatsink Plane provided that the solder extends 360 de
Electronics Forum | Thu Jun 24 04:38:31 EDT 1999 | Vinesh Gandhi
Recently, there has been an upsurge in the Pin Hole/Blow Hole problem in our wave soldering process. We are baking the PCBs for 2 Hrs. at 125 degree C. The Wave Soldering profile seems to be O.K. Still the problem is persistent. Can somebody help
Electronics Forum | Fri Dec 07 09:43:04 EST 2001 | Russ Steiner
I have a mixed technology PCB that has SMT all on bottom, TH parts on both sides (Yes, I realize that's bad. Can't be avoided.) We have designed a 10-up panel, 2 x 5 array. There are 50 leads per bd, 500 per panel. How much time is reasonable to a
Electronics Forum | Mon Mar 11 11:11:38 EST 2002 | slthomas
Tahnk you for posting the charts. > > They look > very useful, but I have a silly question: In > reflow problems _ What is "leaching" ? Dissolution of the component metallisation into the liquid solder. _ > What is "Halo effect" ? "...a
Electronics Forum | Thu Sep 26 14:43:43 EDT 2002 | Jim M.
unsure of what solder spec. your working to?.IPC/EIA J-STD-001C, Section 9.2.4 clearly states dull, matte, gray or grainy appearing solders are accpetable depending on your process and if the acceptability of the neaxt paragraph is met.IPC 610 and J-
Electronics Forum | Thu Sep 23 14:58:50 EDT 2004 | C Lampron
EMS-Engineer, Lead free alloys have a very low wetting creep. You probably will not ever get the same type of weting with a LF as opposed to SN 63/37. The question is if it is acceptable. Lead free solder joints cannot be inspected to the same crite
Electronics Forum | Tue Jul 01 17:15:03 EDT 2008 | ronhodgson
I would like an interpretation of a solder fillet on a 5 side termination cap. (Ref: IPC-610, sec. 8.2.2.6). My question pertains to the definition of dimension F, and what constitutes the top of the fillet. Does the top of the fillet end at where
Electronics Forum | Wed Mar 03 06:13:23 EST 2010 | grahamcooper22
The picture shows that the heel of the device lead is not on the pad. Either bad placement or wrong pad dimensions. I imagine most customers would reject this joint as only a small part of the lead is actually in the solder. With no heel fillet the j
Electronics Forum | Mon Jun 11 22:00:19 EDT 2001 | davef
IPC-A-610 uses words to the effect that it�s a Class 2 process indicator, if either: * Entrapped or encapsulated solder balls that are within 0.13 mm [0.00512 in] of lands or connectors, OR * Entrapped or encapsulated solder balls exceed 0.13mm [0.00