Electronics Forum | Tue Dec 04 08:34:07 EST 2007 | davef
We no advice to give you on the topic, but maybe while you're waiting for others to reply, reading a trade journal article on the topic might help. Below is a link to "Pin-in-hole reflow (PIHR) and lead-free solder joints" by David Bernard, Bob Willi
Electronics Forum | Wed Mar 22 01:24:54 EST 2006 | Joseph
Dear all, Referring technical report from Vitronics Soltec, "Pad lifting, fillet lifting and fillet tearing issues in LF soldering". The use of LF solder alloys today has brought about a recurrence of this crack formation, called fillet tearing. The
Electronics Forum | Tue Jan 16 07:07:17 EST 2007 | tk380514
Answers: The component does take solder, no problem We get a full barrel fill with an empty PCB but only on one of the holes, the other hole has so much copper around it. The flux reached the top of the PCB when I tested the empty PCB. The IPC-A-610
Electronics Forum | Wed Aug 10 16:37:35 EDT 2011 | davef
Yes, there are ways to machine process boards like this. The devil is in the detail. In no particular order, your choices are: Process flow #1: * Print chipbonder on the surface mount side for SMT parts * Mount SMT components * Cure adhesive, if r
Electronics Forum | Thu Mar 23 22:26:53 EST 2006 | Joseph
Dear all, Referring comment from Mr. Jack,IPC director certification & assembly technology, the term "fillet tearing" is too broad. Cracks or fractures in the required fillet area, with SnPb or LF alloy and whether you call it tearing or not, is a D
Electronics Forum | Sun Aug 19 15:34:20 EDT 2007 | davef
What are you trying to do: * Improve hole fill? * Reduce PTH voiding? Hole fill: Search the fine SMTnet Archives for stuff like: http://www.smtnet.com/forums/Index.cfm?CFApp=1&Message_ID=36063 PTH voiding: Ideally, there are no voids. We're unawar
Electronics Forum | Wed Oct 12 12:33:11 EDT 2005 | Inds
Hi Everyone, I am trying to site dress PTH holes filled with Nihon solder mixed with SAC solder at the rework station. But what i am seeing is the solder just doesn't melt and I am not able to suck the solder out of the PTH. Has anyone faced this i
Electronics Forum | Sat Aug 18 11:23:10 EDT 2007 | Learn From U
Hi All, Via X-rays, we found solder voids appear on PTH location, especially on Dimm connectors area. We think this should be related to PCB issue as we found solder unable to fill up the PTH hole during bare board testing at wave soldering machi
Electronics Forum | Mon Oct 15 14:36:03 EDT 2018 | davef
The methods of verifying PTH hole-fill. 1 Visual inspection 2 x-ray inspection works very well for inspecting such a connector for voiding and hole fill. View the connector off-vertical, at between 30 and 45 degrees. As always, the solder connect
Electronics Forum | Thu Aug 05 08:04:32 EDT 1999 | Peter Barton
| Hi , | | Could DIP package ( PTH) run through IR Reflow instead of wave soldering? | | Will there be any reliability impact on this package. | | Thanks | | Jack | | Jack, The dip component package material and the packaging process is the sa