Electronics Forum | Tue Mar 25 02:58:24 EDT 2014 | molder
ok.. thanks you so much.. I will buy new dispenser siringe, and I try to rework... I have a questions on desolder and solder a socket 1366 intel on motherboard. I have a rework station Honton hot air and tornado infrared, but i don't know a temperatu
Electronics Forum | Fri May 12 08:50:40 EDT 2006 | Rob
Just come back from Nepcon (electronics show on an obscure little island on the other side of the pond) and had a good chance to look & play with a whole bunch of solder wire. Koki do one that is aprox. 99/0.7/0.3 with 0.03 Cobolt in. They claim th
Electronics Forum | Thu Sep 07 08:50:45 EDT 2006 | Grant
Hi, We have seen a slight rise in failures in a product, and on investigation, the BGA ball has cracked off the PCB. It's below the intermetalic layer in the ball. Reflow otherwise looks good, and the raw components are clean. I am wondering what c
Electronics Forum | Thu Mar 15 06:26:26 EST 2001 | Sal
Sorry for the lack of information provided, I'll try again : Test Points are the one's that are not soldering. The test points are round in geometry, 0.5MM(metric) in diameter with a HASL finish.The test point are no different to the ed through hole
Electronics Forum | Mon Mar 24 20:30:01 EDT 2014 | davef
The "correct" answer is: Use the tests and methods that you used to qualify your solder paste in the first place. That sounds good but might not be all that practical for practicing assembly-types. Here's something that's not as good, but will give
Electronics Forum | Tue Nov 05 09:57:45 EST 2013 | cuperpeter
Hello All, We have a problem with dewetting of solder paste. Problem is most visible on the pads without components (see attached pictures) and occurs randomly, 20% of PCB's. Pcb supplier sent us a cross-section of pads with thickness of Cu, Ni and
Electronics Forum | Mon Jan 22 09:28:57 EST 2001 | Adam
The assembly is HASL finished. The colour of the solder mask is green, ( sorry I dont know the technical name ).The flux is No Clean (Koki JS3000)which is seeing a preheat temp between 90-100degCel. The solder pot is set at 250degCel and is 63/37.
Electronics Forum | Sun Jan 24 14:01:56 EST 1999 | Daniel
| I'm currently planning to do an evaluation of RMA flux solder pastes for mil type applications. Does anyone have any suggestions for vendors to try? I'm especailly interested in pastes that aid application on boards with 20 mil pitch. | "KOKI 95
Electronics Forum | Tue Jan 02 08:11:21 EST 2007 | Rob
Try using a solder like S03X7C from Koki, which uses cobalt to prolong the tip life & also a wire wool type dry wipe instead of a wet sponge.
Electronics Forum | Wed Aug 26 05:24:42 EDT 2009 | ghepo
Ok Eric, finally we know that the problem should be the PILLOW (sincerely, your photo is not very clear) and not the crack of the joint. There is a big difference on the failure mode of the two defects... If the problem is realy a pillow I only ca