Electronics Forum | Thu Aug 29 06:48:01 EDT 2002 | yngwie
I have seen several Imm Ag pad on the assembled board which have a copper colorleaching through the silver plating This happened on the pad which was not deposited with paste during the assembly process. Don't know if it is a problem, but we only
Electronics Forum | Wed Feb 01 12:20:16 EST 2006 | cvoyles
Hi Bruno, I am an equipment reseller in business since 1994. I have a Smart Sonic MG3000 ultra sonic stencil cleaner in inventory. It is a stainless steel model with Delta Sonics brand ultra sonic generator. It is the guillotine type that raises a
Electronics Forum | Fri Jul 14 14:05:55 EDT 2006 | nodlac
Additional to Dave F.... A potato has Iron @ 2.75mg and Magnesium @ 55mg. The leaching of these two meatls could contaminate the solder pot and taint the solder. ----------------------- Additional to my additional..THE SOLDER POT POTATO BATTERY...A p
Electronics Forum | Fri Mar 24 11:12:06 EST 2006 | patrickbruneel
You�re a good man Rob and a good patriot, you defend your governments decisions even if they're wrong. Isn't the WEEE directive aimed at preventing electronics ending up in a landfill? This immediately takes away the leaching arguments and is a great
Electronics Forum | Sat Apr 21 08:26:57 EDT 2007 | Cmiller
Has anyone experienced a problem with conformal coating adhesion to IS-410 boards? We are having problems with one suppliers boards. IS-410 boards from other suppliers are fine and all FR-4 boards that I have looked at are fine. We are using Conap
Electronics Forum | Tue Aug 07 19:32:40 EDT 2007 | davef
Zinc from the brass diffuses into the solder and reacts with tin causing dezincification. Dezincification is a specific type of de-alloying, or selective, leaching corrosion of brass fittings. This type of corrosion selectively removes zinc from th
Electronics Forum | Sat Mar 14 09:12:59 EDT 2009 | davef
First, there is no good justification for getting solder on gold fingers. Second, it is well known that solder on gold fingers is unacceptable. So, shipping boards with that condition indicates sloppy quality practices at your CM. Third, that being
Electronics Forum | Sun Jul 24 16:10:16 EDT 2011 | davef
As a shot in the dark response to a hopelessly vague question .... Back in the old days, we'd see corrosion of metal parts after DI water washing when our water was on the high-end of the resistivity range, usually after we received fresh tanks from
Electronics Forum | Tue Apr 19 16:20:05 EDT 2016 | davef
Don't blame it on the poor paste thickness requirement [although I might go on to argue that it's could be a contributor to the issue]. Most likely you're the problem. About 70% of the time solder on gold fingers is caused by poor cleaning of screen
Electronics Forum | Thu Feb 27 16:23:37 EST 2020 | dwl
http://www.circuitnet.com/news/uploads/3/Comparing-Soldering-Results-of-ENIG-and-EPIG-Post-Steam-Exposure.pdf Years ago, I battled this problem. ENIG PCBs reflowed with active WS flux. We built one side, and then washed them because they were going