Electronics Forum | Sat Apr 14 09:28:58 EDT 2007 | davef
When soldering a component to a board, the solderability protection on the component combines with the solderability protection on the board and the solder to form an alloy. This alloy is unique for that combination of solder and solderability protec
Electronics Forum | Wed Feb 03 23:40:26 EST 1999 | Chris G.
| Does anyone know if I will have problems soldering surface mount components to an all hard gold plated PC board. We want to use hard gold similar to gold used for edge fingers because our customer is concerned about wear and conductivity of connect
Electronics Forum | Tue Apr 26 15:21:11 EDT 2005 | russ
Sounds to me like they are thinking since they have a gold board that it must be processed lead free. This kind of thing is happening all over since OEMs are starting to think about pb free and sending their purchasing and engineering to these semin
Electronics Forum | Tue Mar 21 20:25:30 EST 2000 | Dave F
John: What�s the matter? Free gold � good thing for you, bad thing for your supplier. :^) Pre-tinning of gold plated leads is important to: � Prevent gold embrittlement of the solder joint � Determine if the leads are solderable prior to assembly (
Electronics Forum | Thu May 02 09:33:30 EDT 2013 | 15009
Looking for advice on soldering lead free paste to a board with very heavy gold plating. I have learned from the Customer that this is HARD GOLD and that it is 10-20 Micro Inches Hard Gold over 100 Micro inches of Nickel. When we reflowed the solde
Electronics Forum | Mon Dec 13 10:12:45 EST 1999 | John Thorup
Hi Dennis The gold plating on a circuit board is present to protect the nickle plating from corrosion. The layer is so thin that as it goes into solution in the solder it constitutes only a small percentage of the total joint. It is commonly accept
Electronics Forum | Thu Jun 09 06:15:17 EDT 2005 | Clampron
Joseph, We have all been using lead free components for some time. Many passive already have a Pb free plating and we have not seen catastophic failures on them. From the information I have seen, I think this should be OK (with the exception of BGA'
Electronics Forum | Thu Sep 16 17:22:16 EDT 1999 | DaveJ
We have some SMT components with gold plated leads. They're actually LCC led packages. A good solder alloy to use would be Indium / Lead to reduce tin dissolution into the gold and avoid the resultant brittle intermetallic compound. However, a recomm
Electronics Forum | Thu Sep 16 18:07:16 EDT 1999 | Earl Moon
| We have some SMT components with gold plated leads. They're actually LCC led packages. A good solder alloy to use would be Indium / Lead to reduce tin dissolution into the gold and avoid the resultant brittle intermetallic compound. However, a reco
Electronics Forum | Thu Sep 16 20:55:35 EDT 1999 | Dave F
| | We have some SMT components with gold plated leads. They're actually LCC led packages. A good solder alloy to use would be Indium / Lead to reduce tin dissolution into the gold and avoid the resultant brittle intermetallic compound. However, a re