Electronics Forum | Fri Jan 04 15:42:03 EST 2002 | nwyatt
There are several implications: - some lead free alloys do not form an acceptable solder joint when used with lead contaning paste. (ie. Bismuth) - if you use both lead free and lead containing components, you will have different solder joint compos
Electronics Forum | Fri May 28 17:44:51 EDT 1999 | Glenn Robertson
| I discovered that we have some gold plated (30 mico in.) through hole connectors which were Paste In Hole soldered (60 sec at reflow) on a HASL PCB. Do we have an embrittlement reliability issue? The calculated volume % of gold in the joints is abo
Electronics Forum | Fri May 28 17:30:35 EDT 1999 | Dave Clements
I discovered that we have some gold plated (30 mico in.) through hole connectors which were Paste In Hole soldered (60 sec at reflow) on a HASL PCB. Do we have an embrittlement reliability issue? The calculated volume % of gold in the joints is about
Electronics Forum | Thu Aug 13 16:46:13 EDT 2009 | snsmt
Hello Everyone, I have noticed that everytime that we have ran a PCB with fine pitch components (or even 0603s), there are little white strands on the leads or on top of the components. It occurs on both lead and lead free solder. We usually soak
Electronics Forum | Tue Jun 06 11:47:33 EDT 2017 | stevezeva
Hi Zac, was that board finished with tin/lead HASL or leadfree/HASL? Also what type of flux were you using? Just because a board is fresh out of sealed packaging doesn't necessarily mean that it's going to solder well. The picture that I've attached
Electronics Forum | Mon Apr 05 16:12:16 EDT 2010 | dyoungquist
We are installing via reflow soldering a crystal that has 2 pads, 1 each end. They are flat pads on the bottom of the part with a small area of the pad looping around and up the side of the crystal on the end. Inspection of the cyrstal under a 40X
Electronics Forum | Mon Oct 22 05:04:08 EDT 2007 | jkhiew
Hi, Recently we have encountered solder wicking on components termination (total of 13 pcs of components on one pcb)with Ag/Pd finishes during lead-free reflow soldering. The pcb is LF HASL surface finish and LF solder paste composition is SAC305.We
Electronics Forum | Mon May 18 20:57:06 EDT 1998 | Earl Moon
.025" pitch so the only problem we run into is too much HASL on the adhesive side causing improper glue dispense. | As Earl keeps saying HASL thickness is hard to impossible to control. I think we need to look hard at OSP's again but then you get in
Electronics Forum | Mon May 18 22:54:04 EDT 1998 | Dave F
.025" pitch so the only problem we run into is too much HASL on the adhesive side causing improper glue dispense. | | As Earl keeps saying HASL thickness is hard to impossible to control. I think we need to look hard at OSP's again but then you get
Products, services, training & consulting for the assembly, rework & repair of electronic assemblies. BGA process experts. Manufacturers Rep, Distributor & Service Provider for Seamark/Zhuomao and Shuttle Star BGA Rework Stations.
Training Provider / Manufacturer's Representative / Equipment Dealer / Broker / Auctions / Consultant / Service Provider
1750 Mitchell Ave.
Oroville, CA USA
Phone: (888) 406-2830