Electronics Forum | Thu Feb 22 04:00:02 EST 2001 | Scott B
We are increasingly being asked to store components for longer and longer periods which we know through experience leads to reduction or total loss of solderability of the parts. 1) What is the industry accepted shelf life of tin/lead plated compone
Electronics Forum | Wed Dec 15 21:29:34 EST 2004 | davef
We�d say that it�s incorrect that ENIG solderability protection cannot be steam aged. It�s true the immersion tin and silver cannot be steam aged. We believe that most of the issues surrounding the poor performance of ENIG after steam aging is attr
Electronics Forum | Thu Mar 24 07:06:06 EST 2005 | davef
There's a lot of comparison tables on the web. Here's one: Properties - Summary [A Winlow Circatex] Attribute||Hasl||Immersion Silver||Immersion Tin||Electroless Pd||OSP||Eless Ni / Imm Au Shelf Life (months)||12||12||12||12||12||6 Multiple Reflows
Electronics Forum | Wed Sep 01 08:27:38 EDT 2004 | davef
Zinc from the brass [Cu3Zn2] diffuses into the tin causing solderability problems. Just 0.001% of Zn in your solder can render it fit for the scrap heap. So, you need a barrier plate between the brass and the tin. Copper or nickel-plating is commonl
Electronics Forum | Tue Aug 07 19:32:40 EDT 2007 | davef
Zinc from the brass diffuses into the solder and reacts with tin causing dezincification. Dezincification is a specific type of de-alloying, or selective, leaching corrosion of brass fittings. This type of corrosion selectively removes zinc from th
Electronics Forum | Mon Aug 28 17:04:52 EDT 2006 | Board House
ImSn - Immersion Tin - Not Recomended- short shelf life ImAg - Immersion Silver - Prefered Surface finsh by most Board houses, Best reworkablility, 12 moth self life, ENIG - Electroless Nickel Immersion Gold - Second Choice for Board Shops, 12 -
Electronics Forum | Mon Apr 26 17:45:26 EDT 1999 | Earl Moon
| | | Earl said, in essence: | | | | | | | Justin is absolutely right ... | | | | | | | | Again, Entek is not much more than a flux coating ... | | | | | | | | Metallic coatings protect best, as we all know - especially those electroplated. Those
Electronics Forum | Tue Mar 20 20:12:32 EST 2001 | davef
In response to a similar question Dennis Fritz [DDFRITZ@AOL.COM] Chair of the Alternate Final Finishes Committee of IPC (5-23d) said ... The Alternate Final Finishes Committee of IPC (5-23d) has nearly completed a round robin "conditioning" study of
Electronics Forum | Thu Aug 31 18:59:55 EDT 2000 | Brian W.
Our customers use OSP, HASL, immersion tin and immersion gold as board finishes. If I recommend a finish to the customer, it is one of the immersion finishes or OSP. Those finishes have the advantage of a flat surface to deposit paste. HASL has va
Electronics Forum | Mon May 18 20:57:06 EDT 1998 | Earl Moon
.025" pitch so the only problem we run into is too much HASL on the adhesive side causing improper glue dispense. | As Earl keeps saying HASL thickness is hard to impossible to control. I think we need to look hard at OSP's again but then you get in