Electronics Forum | Wed Oct 04 16:54:24 EDT 2006 | cw
OK. Thanks!! Lastly, is it the nature of the chemistry that Sn/Pb solder mixed with Pb-free alloy will be getting voids? If so, what's the physic/chemistry behind it?
Electronics Forum | Fri Jul 13 19:35:02 EDT 2007 | hegemon
We have had good success doing pb Free QFN work. Typically for the center pad we use ~68% coverage with 1:1 ratio on the perimeter pad. For the 68% coverage we have tried cross hatch pattern, diagonal stripes, dot series, and most successfully a clo
Electronics Forum | Mon Nov 28 21:37:37 EST 2005 | milroyperera
Hi, What would be the standard band width for Pb-free soldering? As per my knowledge this should be 3cm to 6cm. What is best?
Electronics Forum | Mon Nov 28 09:14:53 EST 2005 | lupo
Just change the flux. I have had bad experience with IF2005
Electronics Forum | Tue Nov 29 08:50:39 EST 2005 | pjc
Band width relates to conveyor speed to achive a 2 second contact time for Sn/Pb wave soldering. A typical conveyor speed is 150cm/min with a band width (contact band width between PCB and solder) of 5cm. Now for Pb-Free wave soldering a longer conta
Electronics Forum | Thu Nov 13 20:48:04 EST 2003 | davef
There a number of studies like this published by component fabricators. Many can be found on the net. For instance: http://www.amd.com/us-en/assets/content_type/DownloadableAssets/Pb-free_Board-level_reliability_study.pdf
Electronics Forum | Sat Nov 26 05:55:04 EST 2005 | milroyperera
Hi, Does any body have the experience with wave soldering a "Gold" plated PCB with SMD assembled on it? I`m experiencing massive bridging,icicles,Shadowing & Skipping. The present soldering angle is 6 deg:,pre heating rate is 2 deg/sec , Dwell time
Electronics Forum | Mon Nov 28 09:46:24 EST 2005 | pjc
I have waved gold (ENIG) boards. That's a pretty hot pot at 260C, wow. I have used 245C with good results. All other parameters look OK a glance. Well, PCB temp looks a little hot too at 130C before pot. 90-100C is typical for most No-Clean flux. At
Electronics Forum | Tue Dec 15 14:38:23 EST 2020 | emeto
I have done it different ways on different equipment. 1. Remove alloy one from the machine. Add alloy two only. and use it.For next board, do the same. 2. There are machines with separate sections for PB and PC-Free, so pots are away from each other
Electronics Forum | Tue Aug 22 09:49:39 EDT 2000 | galltp
Dr. Lee, We have seen a small decrease in shear strength for Pb/Sn plated components attached with Sn/Ag/Cu solder compared to components with a Pb-free finish. With the jump in the cost of Pd, we are struggling to define a practical Pb-free