Electronics Forum | Fri Feb 22 13:48:27 EST 2013 | cyber_wolf
I have been told that stencil nano-coatings are rain-x in a different container. I guess I half believed it until I opened up a sample the other day. It smells EXCACTLY like rain-x. For those of you that have never smelled rain-x it has a very distin
Electronics Forum | Fri Oct 18 08:54:18 EDT 2013 | emeto
Hege, the Nano coating goes on the opposite of the squeegee side of the stencil. I don't know if the cleaning paper is able to remove it little by little with the time, but I never refreshed my stencils with Nano coating and they work just fine. How
Electronics Forum | Fri Jun 17 16:29:05 EDT 2011 | markhoch
Has anybody else tried using stencils coated with Nano ProTek? I did find that I could reduce my cleaning frequency and squeegee pressure, which should help to increase stencil life, but I'm finding that it seems to wear off quicker than I thought i
Electronics Forum | Fri Jul 22 13:17:49 EDT 2011 | ehughes
I would be careful with trying Rain-X. Rain-X is a silanol treatment that is not durable. That is why you need to reapply it on a windshield many times. Also you could contaminate the paste as it will come off the stencil during the printing. From
Electronics Forum | Wed Nov 15 12:52:21 EST 2017 | georgetruitt
IMO – Look into nano-coatings for your stencil and radius all square apertures This should help out with solder paste releasing from the stencil helping with insufficient solder QFN LGA aperture design, try a stencil cut with a few different apertur
Electronics Forum | Thu Oct 17 21:13:35 EDT 2013 | hegemon
But where does it go, that it needs to be refreshed or replenished on the stencil? Does that "just like wax" product wind up in my solder joints, no matter how small the percentage, and would it then qualify as a contaminant? I heard there are some (
Electronics Forum | Thu Sep 09 20:48:12 EDT 2021 | laserstencils
I do not know of a way to measure the nano-coating. However, it is easy to check if it is still on the stencil. Simply use a 'sharpe' pen and try and mark the bottom (PCB) side near any openings. If it easily marks, then the nano is no longer present
Electronics Forum | Thu Mar 22 10:07:48 EDT 2012 | hussman
We chose the MPM over the DEK. We did real world comparison in our factory with both machines almost side by side last year. MPMs offer a real windows based software that basically takes the operator out of the equation. Besides the basic screen p
Electronics Forum | Tue Aug 20 09:26:36 EDT 2013 | proceng1
I believe that Rain-X contains silicone and Nano-ProTek solution does not. I did speak with a field service guy for Nano-Protek and he told me the special coating test pen that they offer is just a sharpie with their logo on it. Thats how I test to
Electronics Forum | Mon Mar 18 11:25:24 EDT 2013 | cyber_wolf
I was at an SMTA meeting Friday. One of the topics of discussion was nano coatings. 1. Nobody wants to talk about where the coating goes as it wears off. 2. There are different types of nano coatings : Chemically bonded which involves a special bon