Electronics Forum | Fri Jan 10 14:49:20 EST 2020 | emeto
Steve I did investigate the transparent nano coat before for performance. We examined 3 different assemblies based in design criteria. In more simplistic designs it is not worth having it. On more challenging designs it is worth. It proved to have be
Electronics Forum | Fri Oct 18 08:54:18 EDT 2013 | emeto
Hege, the Nano coating goes on the opposite of the squeegee side of the stencil. I don't know if the cleaning paper is able to remove it little by little with the time, but I never refreshed my stencils with Nano coating and they work just fine. How
Electronics Forum | Wed Mar 18 11:27:24 EDT 2020 | slthomas
I am about to order a stencil and I can already see that I'm going to have issues. I'm hoping someone has a recipe for this scenario that we haven't tried yet. The parts are 16 mil pitch bga's, the pads are NSMD (10 mil dia. with 12.6 mil mask open
Electronics Forum | Fri Jul 22 10:43:00 EDT 2011 | cyber_wolf
Rain X goes on windshields. Nano coating goes in the garbage. Order your stencils correctly from a reputable stencil house and fugetaboutit.
Electronics Forum | Fri Jan 10 14:41:02 EST 2020 | slthomas
I'm wondering if anyone has ever done a before/after test on the wipe-on type to see if it's any better. The factory applied stuff has been a game changer for us and as already stated, has the added benefit of a dye to indicate that it's still ther
Electronics Forum | Mon Mar 18 11:25:24 EDT 2013 | cyber_wolf
I was at an SMTA meeting Friday. One of the topics of discussion was nano coatings. 1. Nobody wants to talk about where the coating goes as it wears off. 2. There are different types of nano coatings : Chemically bonded which involves a special bon
Electronics Forum | Wed Nov 15 12:52:21 EST 2017 | georgetruitt
IMO – Look into nano-coatings for your stencil and radius all square apertures This should help out with solder paste releasing from the stencil helping with insufficient solder QFN LGA aperture design, try a stencil cut with a few different apertur
Electronics Forum | Thu Oct 17 21:13:35 EDT 2013 | hegemon
But where does it go, that it needs to be refreshed or replenished on the stencil? Does that "just like wax" product wind up in my solder joints, no matter how small the percentage, and would it then qualify as a contaminant? I heard there are some (
Electronics Forum | Mon Mar 18 16:06:35 EDT 2013 | emeto
The paste is going to roll as before because you have to apply the coating on the bottom side of the stencil. Also the coating that wears out will most probably go to your stencil cleaning paper as that the process wehn you actually have friction wit
Electronics Forum | Wed Sep 08 20:22:38 EDT 2021 | emeto
Hello, do you perform any stencil maintenance? What type of controls do you use? Also interested if you have a way to measure nano coating thickness? Any ideas will be appreciated.