Electronics Forum | Thu Mar 02 16:06:32 EST 2000 | eLDON sANDERS
Gentlemen, I too have been atacked by that "soldering to gold" and will add my 2 cents. I also had parts that would pop off the board when the fillet looked perfect. After lots of pain, experimentation, and sleepless nights, I solved it through a
Electronics Forum | Tue Apr 13 09:11:54 EDT 1999 | Dave F
| We process both tin/lead plated boards and gold plated boards in our surface mount group. I have used Sn62/Pb36/Ag2 solder paste on all gold plated boards to help prevent gold scavaging. To reduce the amount of different solder pastes we have to
Electronics Forum | Wed Aug 04 11:01:46 EDT 2010 | ooskii
I have a question concerning what plating will go into solution during the reflow process. I am soldering a small piece of ceramic (120x180 mils 7 mil thick) onto a flex circuit. I am seeing some fractures that I am sure are being caused by handlin
Electronics Forum | Wed Feb 02 20:53:34 EST 2000 | Dave F
Dennis: Several points: 1 If you're talking AlphaLevel process (?): � Good solderability, as HASL, even no-cleans bite well. � Planarity, uniform deposit, no bridgin� of FP. � Doesn't store as well as NiAu ... LT 6 months sealed � Very sensitive t
Electronics Forum | Thu Apr 22 17:19:57 EDT 1999 | JohnW
| | We process both tin/lead plated boards and gold plated boards in our surface mount group. I have used Sn62/Pb36/Ag2 solder paste on all gold plated boards to help prevent gold scavaging. To reduce the amount of different solder pastes we have t
Electronics Forum | Tue Sep 21 13:10:10 EDT 1999 | Dave F
| Dear All, | | In order to understand the soldering technologies in SMT, I'd like to understand why some cards are soldered and then cleaned, or only soldered whitout water cleaning nor "ultra sound" wavelength. | | I mean that I wonder why we use
Electronics Forum | Wed Sep 22 02:45:23 EDT 1999 | Brian
| | Dear All, | | | | In order to understand the soldering technologies in SMT, I'd like to understand why some cards are soldered and then cleaned, or only soldered whitout water cleaning nor "ultra sound" wavelength. | | | | I mean that I wonder