Electronics Forum | Tue Aug 10 20:22:15 EDT 1999 | Wayne Sanita
Hello, Could be that touchup operators are using too much flux. What are you dispensing flux with. Disposable or refillable flux pens are good to have around. | | | | hello to everybody, | | | | we have a really satisfactory no clean proc
Electronics Forum | Thu Aug 12 09:02:08 EDT 1999 | Gian.D
| Hello, | | Could be that touchup operators are using too much flux. What are you dispensing flux with. Disposable or refillable flux pens are good to have around. | |Good! could you suggest some suppliers name or address or web site or e.mail...
Electronics Forum | Tue Aug 10 05:51:03 EDT 1999 | Gian.D
| | hello to everybody, | | we have a really satisfactory no clean process, both smt/reflow and wave soldering, but we get troubles with defects rework; | | does anybody know how to eliminate flux residues or how not to produce them during rework op
Electronics Forum | Mon Jul 01 00:09:47 EDT 2002 | Ben
Hi all How can I clean the white residue between QFP 0.5 mil Pitch? The white residue was created from mistake adding liquild No-clean flux Lonco 23F for reworking clean board. I can clean almost of it by using EC7M cleaning solvent except between
Electronics Forum | Mon Jul 01 15:29:56 EDT 2002 | pjc
I have used a heat gun and found it effective at burning off these residues. Also, check the fine SMTnet archives.
Electronics Forum | Mon Jul 01 22:24:10 EDT 2002 | Por
Thanks for your advise Normally, We do not add any liquid flux (clean or No-clean) during touch up process but this case is an error. Lonco 23F is Nc flux. but our board is clean. However, there are 6 boards that found the white residue and our
Electronics Forum | Tue Jul 02 12:33:32 EDT 2002 | Mike Konrad
We have had success removing white residue. A change of chemical (PCB-Wash or Vigon A200) have a good track record in removing white residue. As Dave stated, we (and others) operate a contract cleaning service. Contact me offline and I�ll provide
Electronics Forum | Mon Jul 01 22:39:28 EDT 2002 | davef
Now, don't be so fast to give-up on those guys. Many saponifier suppliers offer cleaning services for situations like yours. Contact: * Kyzen * Envirosense I seem to remember a similar thread, in the past six months, where our old friend Mike Kon
Electronics Forum | Mon Jul 01 20:44:17 EDT 2002 | davef
Actually, the white res were caused by the water carrier in your Lonco 23F reacting with the res from the nc flux used to solder the component in place. Comments are: * Some nc flux res are cleanable, some are not. Your supplier [Alpha?] can probab
Electronics Forum | Wed Feb 26 22:22:00 EST 2003 | Grant Petty
Hi, The guys here have some boards that have been reworked however as we use no-clean paste we are getting the white residue after ultrasonic cleaning. We are using an alcohol based cleaner in the ultra sonic cleaner. Does anyone have any ideas, or