Electronics Forum | Tue Jun 02 17:36:43 EDT 1998 | Chris Fontaine
| | We have experienced poor adhesion of acrylic conformal coating to plastic bodied IC�s. The observed symptoms of this are a blistering or lifting of the coating at the surface of the component, although peel testing has revealed that this is not
Electronics Forum | Wed Jun 03 15:22:12 EDT 1998 | Greg Curler
| | We have experienced poor adhesion of acrylic conformal coating to plastic bodied IC�s. The observed symptoms of this are a blistering or lifting of the coating at the surface of the component, although peel testing has revealed that this is not
Electronics Forum | Tue Jun 02 18:01:47 EDT 1998 | Earl Moon
| | | We have experienced poor adhesion of acrylic conformal coating to plastic bodied IC�s. The observed symptoms of this are a blistering or lifting of the coating at the surface of the component, although peel testing has revealed that this is no
Electronics Forum | Sat Apr 21 08:26:57 EDT 2007 | Cmiller
Has anyone experienced a problem with conformal coating adhesion to IS-410 boards? We are having problems with one suppliers boards. IS-410 boards from other suppliers are fine and all FR-4 boards that I have looked at are fine. We are using Conap
Electronics Forum | Wed Apr 19 16:24:11 EDT 2006 | patrickbruneel
Here's an other option called seal and peel http://www.interfluxusa.com/misc.html
Electronics Forum | Wed Apr 19 11:50:05 EDT 2006 | amol_kane
Hi BJ, Everyone's favourite answer...it depends! If the volume if large, masking boots will save you both, time and money in the long run. Custom boots are relatively expensive to buy, but they pay themselves over time by savings on masking tape. ma
Electronics Forum | Sun Apr 05 12:30:22 EDT 2009 | qualityguy
Forum: Has anyone experience conformal coat peeling after HASS and the failure mechanism being low surface energy attributed to the solder mask?
Electronics Forum | Tue Apr 07 15:36:15 EDT 2009 | gtemkin
Most of the conformal coating manufacturers recommend verifying the compatibility of their coating with the solder mask, so it's no surprise that occassionally there will be such issues. Are you sure your conformal coat is completely cured? If your
Electronics Forum | Tue Apr 07 20:06:27 EDT 2009 | davef
We doubt that HASS has much to do with your conformal coat peeling. Sure, poor wicking [low surface energy] could cause the issue that you see. Here are links to a couple of good [no formulas or differential equations] articles on surface energy: * h
Electronics Forum | Wed Mar 20 09:54:11 EDT 2013 | patrickbruneel
Seal and peel would be the solution to your curing time problem. It’s a thermoplastic hot melt which air cures as quick as 30 seconds. http://www.interfluxusa.com/Datasheets-PDF/Seal-and-Peel-(DSRev08).pdf