Electronics Forum | Fri Jun 01 06:40:39 EDT 2012 | umar
Hi Norman... Thansk on yoru input, actually my adhesion test conduct is after pass of IC test. MY IC Test is shown a good result but when go into teh Test adhesion coating then during peel off test my board was failed.
Electronics Forum | Thu Apr 09 21:15:43 EDT 2009 | qualityguy
Interesting, A north American Solder resist firm stated the same thing to a degree. They said altering the resist cure profile can effectively change the surface energy thus making the surface more conducive to conformal coat adhesion. At in coming
Electronics Forum | Thu May 12 08:24:05 EDT 2005 | patrickbruneel
Amejia, If your application is strictly conformal coating and no heat is applied to the board, the product seal and peel would be the solution see link http://www.interfluxusa.com/misc.html This product solidifies immediately on cooling The only dra
Electronics Forum | Thu Apr 09 06:28:11 EDT 2009 | qualityguy
We have different Solder mask 'gloss' and 'satin' the gloss has a surface energy =40 dynes. The test evidence to date is strong correlation between surface energy, mask type, HASS failure
Electronics Forum | Thu Apr 09 18:55:49 EDT 2009 | gregoryyork
seen it many times before when the resist is not cured at manufacturing. get PCB man to check with K type thermal couple that boards ARE in fact cured. this is normally 155C ON board temperture not oven setting Cheers Greg
Electronics Forum | Thu Apr 09 21:21:11 EDT 2009 | qualityguy
Hello, another SME is saying the solder resist cure level is suspect. I have had a industry SME make reference to this too. Adjusting the cure of the resist changes the surface energy
Electronics Forum | Wed May 09 03:13:06 EDT 2012 | umar
I had send my coating board to the test lab for adhesion coating test. 3 times send, the result 3times fail. The coating chemical use is Humiseal 1B31. The process is clean the boards at washing process use the Vigon A200 saponifier mix with DI wate
Electronics Forum | Tue Dec 08 17:55:51 EST 1998 | Dave F
1. What is the best way to remove polyurethane conformal coating from selected areas? Your conformal coat material supplier is best equipped to tell you how to remove the coating. Polyurethane conformal coating is not easy to remove. Without in-pu
Electronics Forum | Thu Apr 09 06:22:27 EDT 2009 | qualityguy
We aware of the extend time for cure, and in the CA activity we tried plasma etch and expose the sample to the current process, a screen test of 4 cycles -50C to 125C and the CC held in place. Std IPC tape test passed in current process and modifie
Electronics Forum | Tue Apr 14 17:39:34 EDT 2009 | gregoryyork
Sorry been away for a while. It is actually due to high boiling solvents or plasticizers leaching from the porous resist that kills the cure as it puddles out and has nothing to adhere to. We do have some wipes to check the cure and are looking to ma