Electronics Forum | Tue Nov 15 22:33:16 EST 2022 | kumarb
Yes, solderbility. I recall one case of a vendor we met at a past HK electronic fair. Pricing was ok, we selected them and ordered a batch of boards. After a few months of leaving the PCBs in a sealed package (vacuum), we attempted to use the PCBs. W
Electronics Forum | Wed Nov 16 21:35:07 EST 2022 | stephendo
" so I wander what can I do to save them?" The boards or management? Seriously I think this is more of a management issue than a technical issue. We can suggest what to do but if management does not accept that solution then it won't work. I'm not s
Electronics Forum | Mon Jan 18 10:01:16 EST 1999 | John W
| | | | Folk's, | | | | | | | | I'm looking for information of how long you cna store a gold finish PCB before building it. I know there are problems with the gold disappearing into the underlying nickle over time / temperature etc but exactly how l
Electronics Forum | Tue Jan 19 11:12:41 EST 1999 | Dave F
| | | | | Folk's, | | | | | | | | | | I'm looking for information of how long you cna store a gold finish PCB before building it. I know there are problems with the gold disappearing into the underlying nickle over time / temperature etc but exactly
Electronics Forum | Fri Aug 01 08:10:29 EDT 2008 | scotceltic
Has anyone come across a standard or study (JEDEC, IPC) where it has the recommended shelf life outside of a dry box for immersion silver coated PCB's to prevent oxidation from affecting the soldering process (Both reflow and Wave). I know it will
Electronics Forum | Sun Aug 03 08:27:41 EDT 2008 | davef
IPC-4553, Specification for Immersion Silver Plating for Printed Circuit Boards, 1.4.1 Solderability. This primary function of IAg is to provide a solderable surface finish, suitable for all surface mount and through-hole assembly applications and wi
Electronics Forum | Wed Sep 01 08:27:38 EDT 2004 | davef
Zinc from the brass [Cu3Zn2] diffuses into the tin causing solderability problems. Just 0.001% of Zn in your solder can render it fit for the scrap heap. So, you need a barrier plate between the brass and the tin. Copper or nickel-plating is commonl
Electronics Forum | Fri Jan 11 11:14:14 EST 2002 | leedianeh
I am going to be using large numbers of silver immersion PCB's for assembly. I am concerned about long term storage ( shelf life )and handling prior to placement/assembly. The recommended 'shelf life' appears to be 6 months but obviously this will
Electronics Forum | Fri May 15 21:59:42 EDT 1998 | Earl Moon
| Hi, | There has been a lot of disputes in our company | about changing present HASL to another Finishing | which can provide more flatter pad surface in fine | pitch applications. ( perhaps Ni/Au, OSP ) | The target is to reduce solder defects, t
Electronics Forum | Wed Feb 14 15:54:18 EST 2018 | cbart
do you see signs of contamination or oxidation? if not why not just send them to the board house and have another OSP coating layer applied?
Products, services, training & consulting for the assembly, rework & repair of electronic assemblies. BGA process experts. Manufacturers Rep, Distributor & Service Provider for Seamark/Zhuomao and Shuttle Star BGA Rework Stations.
Training Provider / Manufacturer's Representative / Equipment Dealer / Broker / Auctions / Consultant / Service Provider
1750 Mitchell Ave.
Oroville, CA USA
Phone: (888) 406-2830
winsouce.jpg)