Electronics Forum | Fri Jul 09 18:36:48 EDT 2010 | rway
We don't use flex pcbs but have the same issue here. Most of our pcbs are HASL finish. I have looked at silver and gold immersion and both look really good under my color camera on my AOI. However, gold is more pricey. There is no additional cost
Electronics Forum | Wed Jan 24 11:27:54 EST 2007 | bradlanger
We have been using SN100C lead free hasl for over a year now with good success. It is very solderable and has good shelf life. You do have to make sure the finish gets applied to the correct thickness. If the lead free hasl finish is not applied thic
Electronics Forum | Wed Dec 09 14:36:26 EST 1998 | Earl Moon
| Hi, I know for sure that by controlling temp. and humidity | conditions in SMT assy lines room, one gets advantage in | screen printing, adhesive dispensing, and pick&place | machines mainteinance. Does any one have any advice on why | else is a c
Electronics Forum | Mon May 18 20:57:06 EDT 1998 | Earl Moon
.025" pitch so the only problem we run into is too much HASL on the adhesive side causing improper glue dispense. | As Earl keeps saying HASL thickness is hard to impossible to control. I think we need to look hard at OSP's again but then you get in
Electronics Forum | Mon May 18 22:54:04 EDT 1998 | Dave F
.025" pitch so the only problem we run into is too much HASL on the adhesive side causing improper glue dispense. | | As Earl keeps saying HASL thickness is hard to impossible to control. I think we need to look hard at OSP's again but then you get
Electronics Forum | Sun Mar 01 15:52:13 EST 1998 | Earl Moon
| From several months I am investigation about the VOIDS PERSENCE and his important as reliability. | One question now is : | It is possible that on the BGA components the voids are already present into the balls, before the mounting on the pcb ? | I
Electronics Forum | Sat Nov 14 08:58:38 EST 1998 | Earl Moon
| I keep hearing about polyimide stencils, but what are they like in terms of registration and aperture accuracy? | You are hearing about polyimide as in polyimide film as Kapton (TM Dupont). This material is the stuff of flex and rigid/flex circuit
Electronics Forum | Tue May 26 20:18:09 EDT 1998 | Justin Medernach
| | | | I'm reviewing my board fab spec. It calls for a minimum SnPb thickness of 50 microinches on HASL PWB's. I've looked at other specs that call out anything from 30 to 80 microinches, and others that just say the copper pad must be covered and
Electronics Forum | Mon Apr 26 11:04:53 EDT 1999 | Dave F
| | Earl said, in essence: | | | | | Justin is absolutely right ... | | | | | | Again, Entek is not much more than a flux coating ... | | | | | | Metallic coatings protect best, as we all know - especially those electroplated. Those coatings chemi
Electronics Forum | Wed Dec 22 01:39:06 EST 2010 | boardhouse
Hi Johan, As a Asian board supplier - I would not recommend using Lead free hasl on any product that has BGA, you would be just looking for issues, flatness being the main. I agree with one of the other replies - Your purchasing dept. should not be
Products, services, training & consulting for the assembly, rework & repair of electronic assemblies. BGA process experts. Manufacturers Rep, Distributor & Service Provider for Seamark/Zhuomao and Shuttle Star BGA Rework Stations.
Training Provider / Manufacturer's Representative / Equipment Dealer / Broker / Auctions / Consultant / Service Provider
1750 Mitchell Ave.
Oroville, CA USA
Phone: (888) 406-2830
.jpg)