Electronics Forum | Thu Jun 04 09:53:31 EDT 1998 | Dave F
| I have gold fingers that I want to mask when running over the wave without pallets. They're on the leading edge of the board. I recall seeing rubber boots that slid onto the fingers to mask them. Pop 'em on before the wave; pop' em off after and
Electronics Forum | Wed Mar 16 16:02:55 EST 2005 | Dreamsniper
Hi, Need your help. Easy one. How do you evaluate Spot-on Mask, those that are peelable and used for wave soldering and conformal coating? thanks and regards,
Electronics Forum | Mon Mar 20 15:48:52 EST 2000 | Shane Lay
We are planning on converting to a no-clean soldering chemistry and will need to replace our water soluble liquid solder mask as a result. Does anyone know of a dispensable, "peelable" solder mask I can evaluate? It would be nice to find one that i
Electronics Forum | Sat Apr 04 15:38:10 EST 1998 | Sam Forman, MicroCoat Technologies
| I will be starting a conformal coating process soon, I am looking for any pointers on | 1) Best method for masking components, tape mask, liqued mask | 2) Which is best Spray or Dip? | 3) Compatiblity with no clean solder paste (flux residue) |
Electronics Forum | Thu Jan 28 10:09:51 EST 1999 | Charles Stringer
| | | | Greetings, | | | | | | | | Can anyone tell me what temperatures pcb's should have when coming out of a forced convection reflow oven and out of a wavesoldering machine. | | | | Also, is there any danger of the pcb's giving off some kind of g
Electronics Forum | Fri Feb 22 18:36:36 EST 2013 | austinpeterman
Has anyone experienced bridging on topside (solder destination side) surface mount devices after wave soldering? We x-rayed 100% of the placements after smt re-flow with no issues. When the same placements were x-rayed after the tht wave solder pro
Electronics Forum | Wed May 03 15:00:44 EDT 2006 | patrickbruneel
It all depends on process, design and environment in which the contacts are used. Both have excellent conductivity characteristics Both don't oxidize over time On the other hand gold is much softer then carbon, and after hitting that contact a gazil
Electronics Forum | Fri Nov 04 13:24:30 EDT 2011 | tombstonesmt
Peelable masking has been our solution here recently. We an automovite customer that requires coating on both sides of the boards with many keep out areas. We are currently building a dispense robot that will apply tech spray wondermask 2218. The won
Electronics Forum | Thu Jul 01 14:47:10 EDT 1999 | Tony
| | | My guess would be trapped flux continuing to be active after soldering. Is the tarnish there immediately after exiting the machine? Do you remove the mask and wash right away? If the solder is reflowing under the mask on the component side
Electronics Forum | Wed Feb 07 21:58:38 EST 2001 | davef
We are reviewing our shelf life policy and have the following items listed as shelf life sensitive: Printed circuit boards, peelable solder mask, solder paste, moisture sensitive parts, multiwire printed circuit boards from Icon or Hitachi, NiCd batt