Electronics Forum | Fri May 14 09:00:35 EDT 2010 | rafacadiz
I attached a RX picture. A lot of voids and micro balls arround the flux residue. What do you think, relow temperature reflow or OSP poor weeting.? I appreciate your comments. Thanks,
Electronics Forum | Wed May 27 16:02:32 EDT 1998 | Chrys
| We recently made the switch to no-clean and the wurface mount is turning out beautifully. However, the wave solder process continues to put up a fight; we are getting a white residue on the surface of the PCB. The residue is not localized to
Electronics Forum | Wed Jul 20 12:48:21 EDT 2016 | adamjs
Hi, is there a reason why washing "no-clean" flux residue off of boards with 1(or 2)-ethoxy-propanol is not a widespread practice? This chemical is more commonly known as Henkel/Loctite/Multicore SC01. I've long known, as I'm sure most people do, t
Electronics Forum | Fri Oct 08 02:31:07 EDT 1999 | Brian
| | | | Hi, | | | | | | | | Help! Could anyone help to enlighten me on this? | | | | | | | | Question: | | | | | | | | If I have a CSP/BGA package of size X by Y and the standoff gap between the component and PCB is Z, What is the maximum allowab
Electronics Forum | Tue Feb 11 12:02:52 EST 2014 | javierec
Process: Batch Cleaner, @16% concentration. Concentration is checked daily. Cleaning after Wave Process. See attached pictures and comment and what you think causes the solder joint to turn grey. i have read post that say the grey dull looking sol
Electronics Forum | Fri Feb 01 03:03:08 EST 2002 | madreindeer
Hi, That is very common in WS pastes.It is white residue (Salt) Usually it�s not dangerous it only looking bad. I think best way would be contact your paste supplier and they should know what would take a stain off if not, change supplier. There i
Electronics Forum | Tue May 18 22:31:05 EDT 2004 | davef
Ionic cleanliness is pretty much meaningless, when discussing nc flux residues. If you do the good solder routine and measure the boards, you'll be in the out-house, because the water in your resistivity of solvent extract tester will turn the res o
Electronics Forum | Mon Jul 16 21:29:03 EDT 2001 | davef
Cleaning RMA with water is bad news. It will turn your solder connections white and remove none of the RMA residues. There was a thread on removing RMA within the past two weeks on SMTnet. Check the fine SMTnet Archives. Additionally, look at M
Electronics Forum | Tue Aug 10 05:51:03 EDT 1999 | Gian.D
| | hello to everybody, | | we have a really satisfactory no clean process, both smt/reflow and wave soldering, but we get troubles with defects rework; | | does anybody know how to eliminate flux residues or how not to produce them during rework op
Electronics Forum | Mon Mar 31 11:10:43 EST 2003 | davef
First, most �thermal shock� recipes are not a reliability test. There is no relationship between the failures seem in these tests and in-use application. These tests show you the failures in these tests. That�s it!!! Second, accelerated life test