Electronics Forum | Mon Feb 20 20:47:59 EST 2006 | davef
We assume your stencil is clean. So, try: * Reduce stencil separation speed. * Reduce squeegee pressure. If the pressure is not proper, excess number of particles are stuffed into an aperture and inner pressure / friction among particles increase, an
Electronics Forum | Tue May 23 09:01:48 EDT 2006 | russ
Seems as though the problem is with PCB and not component? "Solder does not wet to pads, wets to component" What is your board finish? Russ
Electronics Forum | Thu May 25 09:14:04 EDT 2006 | cobar
Print a number of pads of the 0603 on to a ceramic substrate. Then place the 0603 on the paste on the ceramic and refow. If the paste shows no wetting onto the component it will prove that there is a problem with the components solderability.
Electronics Forum | Tue Aug 10 05:32:42 EDT 2004 | praveen_madaan@jabil.com
Hi, Has any body experienced the problem of poor cotacts on HDMI connectors. The connectors pins are gold plated and we see some kind of white residue on the gold pins.How to check if this is a flux residue?We are using No Clean flux in wave solderin
Electronics Forum | Tue Aug 10 07:10:11 EDT 2004 | abraham
Praveen, White powder residue can be produced if you clean the No clean flux residue with isopropyl alcohol. Check whether you are using any IP for local cleaning. In case you want to clean the noclean flux residue ( as per the requirements of conta
Electronics Forum | Mon Jul 29 16:43:55 EDT 2002 | mcm4me
I have a customer with up to 8% scrap from one board supplier and 1% from another supplier for solder dewett and no wet over ENIG finish with mask defined pads. Initially I suspected mask residue on pads because of the no wets but I have come to find
Electronics Forum | Thu Aug 01 08:58:47 EDT 2002 | Rick Lathrop
Good morning Dave F. I am not going to try to touchup the solder pad until I get surface analysis work done, don't want to ruin the evidence. I am getting XPS work done not XRF, XPS is X-ray Photoelectron Spectroscopy and can see very thin films of o
Electronics Forum | Wed Jul 31 08:23:49 EDT 2002 | mcm4me
221C). 2D vision can very effectively detect % pad coverage, I use it on my DEK and this customer has an MPM which I also believe to be capable. Here is another fact, when the customer uses Brand X solder paste the defects due to what they call pad
Electronics Forum | Thu May 25 03:31:17 EDT 2006 | slaine
Hi I manufacture ceramic parts that have a terminations that are palladium/platinum/silver or any combination of the 3. Termination Ink usually consists of 3 main parts the alloy, glass frit and binder. Binder is to help bind everything together whi
Electronics Forum | Tue May 23 21:14:22 EDT 2006 | davef
First, where the temperatures that aare mentioned in the original post measured? Second, it sounds like the PdAg component terminations are not seeing enough heat [your soldering iron touch-up proves this]. Your 232*C peak is the absolute minimum s
.gif)