Electronics Forum | Mon Jun 08 12:42:01 EDT 1998 | Earl Moon
| How do I mechanically/visually inspect BGA devices when they are soldered to a PCB for possible solder, or other, defects as a first step before part removal and further analysis? I have had board failures due to poor soldering--I think? I can pr
Electronics Forum | Tue Jan 15 06:05:37 EST 2002 | Romain
Dear all We have since few weeks problems with BGA solder joint integrity on ENIG finish. Under relatively very flexible of the FR4, the joint breaks between ball and PWB. When we take off the BGA for analysis, some of the pads seem very flat, totaly
Electronics Forum | Fri Oct 08 02:31:07 EDT 1999 | Brian
| | | | Hi, | | | | | | | | Help! Could anyone help to enlighten me on this? | | | | | | | | Question: | | | | | | | | If I have a CSP/BGA package of size X by Y and the standoff gap between the component and PCB is Z, What is the maximum allowab
Electronics Forum | Wed Aug 16 13:52:24 EDT 2006 | russ
Oven settings are meaningless here. What does the board see? It is the paste we are concerned about not what the heaters are running at hehe. These solder balls are at the end of pad, which end? under the part or away from the part. I believe you
Electronics Forum | Wed Jul 24 23:21:26 EDT 2002 | ppcbs
Being in the line of BGA rework and having performed much rework on boards that go into military planes, I can give you an opinion from a practical background rather than an in depth study. Basically BGA's have caused many of my customers big headac
Electronics Forum | Tue Sep 25 13:01:48 EDT 2001 | Hussman
If the flux you are applying by brush is alcohol based, use some alcohol on a few failed PCBs and retest. It souldn't take a lot of flux to reflow the balls to a pad that's already covered with solder and flux from the first BGA - unless you are cle
Electronics Forum | Wed Dec 23 11:11:07 EST 1998 | john watt
| | I have been developing a BGA Process and are having problems with a 310 IO PBGA reflowing. I am achieving good wetting exept 2 to 5 balls on the outer perimeter I have a good profile my air flow is set per mfg spec, the strange thing is that it d
Electronics Forum | Tue Mar 13 16:05:30 EST 2001 | rob_thomas
Hi, can you definitely attribute the 30%yield to poor bga soldering? What is your high flyer defect encountered on the failed boards.Is this ICT ,flying probe ,functional test yield? Can you determine a defect pattern? Did your subcontractor provided
Electronics Forum | Fri Dec 18 10:18:55 EST 1998 | Dave F
| I have been developing a BGA Process and are having problems with a 310 IO PBGA reflowing. I am achieving good wetting exept 2 to 5 balls on the outer perimeter I have a good profile my air flow is set per mfg spec, the strange thing is that it doe
Electronics Forum | Tue Mar 13 14:17:00 EST 2001 | blair
Thanks a lot for the response 1) there are 8 BGA on this board 6 PBGA, 1 TBGA and 1 ESBGA (metal lid). They are dispersed over the board (approx 11"* 14") 2) Is there a tool to use to understand pitch/bump size and stencil aperture (optimized)? 3) Y