Electronics Forum | Tue Mar 25 11:43:48 EDT 2014 | sara_pcb
It is Solder Mask on Bare copper, The land finish is HASL as per MIL-PRF-55110G which accepts trace of HASL as acceptable. Wetting is acceptable. regards, R.Saravanan
Electronics Forum | Fri Jun 02 09:31:26 EDT 2000 | C.K.
Okay, there's a debate here at my company. We build a card here that, often times, we get batches where there is excess HASL in the VIA hole barrels. Here is the problem that this causes: During the "1st reflow", the excess HASL bleeds out of the
Electronics Forum | Tue May 10 12:11:27 EDT 2011 | scottp
Do you have pictures and/or cross-sections of the non-wet? Is the HASL SnPb or SN100?
Electronics Forum | Tue Mar 15 17:58:56 EST 2005 | darby
Mat, Are you sure you should be using SnPb HASL boards if you are doing prep for lead free? If you aren't actually going to comply with RoHS then fire away. Nearly all of our assemblies are now ENIG and as any re-design comes up on a HASL board it is
Electronics Forum | Thu Sep 21 02:58:45 EDT 2017 | kubabel
Thank You! I will try to go in touch with them...
Electronics Forum | Fri Jun 07 05:08:08 EDT 2019 | gregoryyork
Does look like delam, if its that bad and the board looks like its HASL finish or Silver, it could also be porous absorbing the chemistries of HASL or Nitric from the Silver which will greatly encourage ECM or poor SIR figures or just simply eat the
Electronics Forum | Mon Mar 16 01:06:25 EST 1998 | Victor Ng
Dear all, Recently I have a problem of non-wetting at our wave soldering process. It appears only on the SMT pads for the chip components (at the solder side) of the HASL PCB. With all the same parameters on the wave soldering machine, i
Electronics Forum | Wed Oct 02 00:08:26 EDT 2002 | praveen
Hi, We are using chip components with Silver Pladium coating and finding poor wetting. We are using the water wash solder paste with 2Ag and std. reflow profile. Any suggestion how ti improve the solder wetting for those components. Thanks,
Electronics Forum | Wed Oct 02 00:08:39 EDT 2002 | praveen
Hi, We are using chip components with Silver Paladium coating and finding poor wetting. We are using the water wash solder paste with 2Ag and std. reflow profile. Any suggestion how to improve the solder wetting for those components. Thanks,
Electronics Forum | Thu Oct 03 10:02:08 EDT 2002 | davef
Your problem is likely not the Pd-Ag surface layers, but the underlying metal to which you need to wet. Either a base metal is: * Contaminated and poorly wettable. OR * A material [eg, Alloy 42 (check with magnet), Kovar, etc] that is inherently dif
winsouce.jpg)