Electronics Forum | Wed Apr 08 11:33:51 EDT 2009 | 1036
2) STD FR4 material with HASL finish, 4 layer board. Reflowed under tin-lead temps with another 4 layer board same time(no delamination problem). 3) We uasualy do not pre-bake board unless board is too old. 4) We do not have the board on hand right
Electronics Forum | Thu Aug 13 13:48:22 EDT 2015 | markhoch
Hi Juan, I think if you check your Solder Paste's Data Sheet, you will find that your Solder Paste can be stored at Room Temperature for up to four weeks. There is no need to put your paste back into the refrigerator after every shift. If it makes
Electronics Forum | Fri Dec 16 03:47:46 EST 2005 | gpaelmo
Anyone have problems wave soldering white tin finish? We are an ems and our customer provides us the pcb's. SMT and TH components on the board. SMT is fine but when we wave solder, wetting to top side is very poor (solder only flows half way up). We
Electronics Forum | Tue May 24 21:48:23 EDT 2005 | steve
You can continue repair and rework with tin/lead solder until 7/06. However!!! Any product still on the shelves overseas after 7/06 will be returned to the USA. Thought? Maybe start repairing with SAC305 now? Also SAC is Tin, Silver and Copper. No Ni
Electronics Forum | Thu Jun 03 17:43:34 EDT 2004 | g2garyg2
Hi Doug, Read your inquiry. My company PRO-MATION has some exciting technologies available for both top side and bottom side selective laser soldering. Our work cells are great for low volume / high mix environments and are capble for both Tin Lead
Electronics Forum | Sat Dec 13 17:46:27 EST 2008 | ysutariya
If you're military then you're probably just needing standard 130Tg FR4 and tin-lead finish. I would check two things: 1. Bake temperature: Isola recommends 300F for 4 hours to drive moisture out. Lower baking temperatures do not require a linea
Electronics Forum | Fri Apr 21 14:58:04 EDT 2023 | rgduval
I mean...there are a ton of possibilities for bridging on selective solder before you ever get to alloy purity. Are the bridges happening consistently in the same spot? Are the leads too long? Can you modify the approach/exit/peel off to address? Wh
Electronics Forum | Wed May 18 14:58:05 EDT 2005 | splice
Hi, I am having some PTH non wetting issues. Setup and chronology of events is explained: Set Up; Part: 1 MM pitch connector 378 pins Solder: Kester Ultra Pure 63/37 solder Pot; 250 C pre heat; Peak 94C top side Flux: Qualitek 775, Fluxer: foam T
Electronics Forum | Fri Mar 21 15:51:23 EDT 2008 | g2garyg2
Thought I would reply and try to assist. PROMATION, my company, also manufactures Diode Laser soldering systems but with this stated we also manufacturer iron tip systems, soft beam systems and hot air solutions. The reasons are simple. Diode Laser
Electronics Forum | Fri Mar 26 09:00:19 EDT 2010 | krish_bala
Thank you Graham for the response. The particular BGA that we currently Bake is a Level 3 BGA, which means the BGA will expire in 7 days after removal. We are currently baking the BGAs once a week for the problem described above. These devices are u