Electronics Forum | Mon May 24 15:45:58 EDT 2004 | mleber
I am interested in how Military / Class 3 manufacturers are handling Gold SMT components. We are receiving an increasing number of tape and reel components that are gold plated. Per J-STD we need to tin all gold components. Are parts being removed fr
Electronics Forum | Fri Jun 19 14:25:24 EDT 1998 | Earl Moon
| | Has anyone had experience with placing BGA on gold plated boards. I thought I read a while ago there was a problem with embrittlment causing cracked joints. If anyone has experience with this your feedback would be great. | | Mike | There has b
Electronics Forum | Tue May 21 13:17:47 EDT 2019 | SMTA-Thomas
2.54 μm [100 μin] gold thickness and all through-hole leads that will be hand soldered regardless of gold thickness” (we automatically solder wash all components which violate this requirement). In all cases we have attempted different no clean flux
Electronics Forum | Thu Sep 16 18:07:16 EDT 1999 | Earl Moon
| We have some SMT components with gold plated leads. They're actually LCC led packages. A good solder alloy to use would be Indium / Lead to reduce tin dissolution into the gold and avoid the resultant brittle intermetallic compound. However, a reco
Electronics Forum | Fri Jun 09 11:18:25 EDT 2006 | kehoem@bellsouth.net
Question; Do you think it's possible that your customer has got his units mixed up & actually means 0.3 micro inches of gold over 0.5 micro inches of Nickel? That is what I said but their vendor says they are building to print which says 80 uM and i
Electronics Forum | Thu Nov 01 04:52:50 EST 2001 | wbu
Hi Brian, yes that�s possible due to the presence of Au in the joint but nothing to worry if the Ni/Au is done properly (means not to much Au in your plating). "rugged" I haven�t noticed yet, that may depend on the definition and maybe the magnifica
Electronics Forum | Thu Jul 27 21:57:16 EDT 2000 | Dave F
Hi Doug: Responding to your questions: � If gold over nickel is self limiting ... You didn�t say whether you gold plating was electroless or immersion. Electroless is not is self limiting. It can plate up to 5 thou. Expect immersion plated gold to