Electronics Forum | Tue Sep 11 22:52:18 EDT 2007 | davef
Here are some options for removing OSP coatings from pads of the BGA substrates. * Leave the substrates in storage for 13-14 months. Shelf life of OSP coating is ~12 months, depending on the product. * Wash the substrates in your aqueous washer. Ea
Electronics Forum | Thu Sep 14 14:18:13 EDT 2006 | Kevin W. Parker
We have begun using a PCB with Organic Surface Protectant. We normally run boards with non orgainic protectant. We can wash these boards with our ultrasonic cleaner using Zestron SC202 and a separate Hot/cold rinse system with an air knife. This r
Electronics Forum | Tue Nov 10 13:31:00 EST 2009 | chris0595
When applying the ECCOBOND E3503-1 thermal adhesive to attach a HB-LED to the slug area of a MCPCB, should the OSP coating on the slug area first be removed? I have heard that OSP coatings have poor adhesion properties so I'm wondering how to do this
Electronics Forum | Thu Sep 14 20:11:19 EDT 2006 | davef
You weren't specific about the OSP that you use. We use Entek Plus CU-106A. Yes, just about everything removes Entek, especially if there's heat involved. Ethone states: * Alcohol strips 70% of the coating * Water removes 15% * Kyzen Lonox only t
Electronics Forum | Thu Jun 22 12:25:07 EDT 2000 | Boca
Jason, What Chrys said! Don't try to run the bottom cooler, tried it in the mid 80's, don't work and don't want it to work. If one side of a fab is maintained cooler than liquidus and the other side into reflow it would have an easy 40C temp diffe
Electronics Forum | Fri Jun 27 10:27:59 EDT 2003 | davef
Since you�re asking the question about proper handling of OSP board, there may still be time to talk you out of using that material. * Cleaning of mis-printed board could cause non-wetting problems. This tends to remove a fraction of OSP coating. 0.3
Electronics Forum | Fri Feb 23 19:27:04 EST 2007 | greg york
true in the olden days, new osp's have excellent thermal stability. they are thinned or removed by organic acids mainly. contrary to believe due to the higher tin content they do tend to work well with lead free better than leaded used to. cheers gre
Electronics Forum | Wed Apr 26 03:32:29 EDT 2006 | saaitk
Hi all, Has anyone any experience they can share with regard to pad dissolution on PTH's on thick boards. We are using lead free SAC305 on both OSP and Immersion silver finishes and are experiencing difficulties when removing and replacing connector
Electronics Forum | Thu Apr 14 06:00:01 EDT 2005 | bryan
The shelf life of immersion silver is 6 to 12 months in good storage conditions. The finish is usually coated with a protective layer that inhibits oxidation (like with copper OSP). Care must be taken when handling the boards as the protective la
Electronics Forum | Fri Mar 07 15:20:11 EST 2003 | davef
O'Connor: IPC-A-610, section 12.4.4 SMT Soldering Anomolies - Nonwetting was added primarily to accomidate OSP boards. Heated flux is used to remove the 'lacguer'. So, you end-up with a copper colored border [or shadow] around the pads, where there