Electronics Forum | Thu Dec 29 09:20:30 EST 2005 | Cmiller
We have tested SN100C and SAC305 in our selective solder machine (Ersa Versaflow). We wanted to test both alloys in the selective first because the investment in filling the pots is minimal. In our initial tests the SN100C alloy appears to be the bes
Electronics Forum | Thu Dec 29 11:43:46 EST 2005 | samir
CMiller, Thanks for the valuable info! We are in the midst of lead-free deployment and need to know good alloy choices at both wave and ERSA. I have heard the same things regarding SAC305's price for bar solder, but don't yet know what the process
Electronics Forum | Fri Apr 04 09:54:39 EDT 2008 | redtiger56
We have been seeing continued difficulty with solder shorts and/or insufficient barrel fill with our Juki selective solder machine while using SAC305. We want to switch to something in the SN100 series, but we do not know enough to seperate the hype
Electronics Forum | Thu Sep 08 09:47:20 EDT 2005 | lupo
I will try with temperature 255 C degrees. The wetting force vs. solder temperature for SAC305 is more than 265 C degrees (the temperature of trials). Thanks for the advise. Regards
Electronics Forum | Fri Dec 30 10:12:27 EST 2005 | Cmiller
Joseph, thank you for your comments. Can I ask what kind of flux you are using?
Electronics Forum | Sun Jan 01 21:02:54 EST 2006 | sumxp
Please elaborate more on hole fill issue.How difficult to optimise the process para?
Electronics Forum | Wed Jan 04 17:06:20 EST 2006 | samir
All I can say about Alpha and their GOTT-DAMN website is THEY SUCK!! I refuse to register to view product literature... for that reason, Alpha Metals, you won't be looked at for my pb-free paste or bar solder evals.
Electronics Forum | Fri Jan 20 08:27:28 EST 2006 | Loco
Just wondering what the companies that are use SN100C are using for reflow (I guess SAC), and especially for handsoldering. Do SAC and SN100C mix? are there any studies proving this?
Electronics Forum | Fri Mar 31 15:49:51 EST 2006 | GS
Hi Marcus, by using SN100C have you seen any tearing phenomena like what shown on the link ? http://www.smartgroup.org/pdf/Defect01.pdf Tnks Regards.........GS
Electronics Forum | Mon Apr 10 13:10:06 EDT 2006 | Marcus
No I have seen Zero hot tears. Thats with water soluble or No-Clean. We have built over 10,000 boards.