Electronics Forum | Fri Jul 10 07:52:15 EDT 1998 | smd
Most of you guys probably wish TH would just go away. Maybe for some of you it has. We have some older but very successful WAN controller boards using TH parts so we get to use automated equipment for this. We have an Amistar CI-3000 inserter that so
Electronics Forum | Wed Jan 19 10:44:23 EST 2005 | russ
Although I have not personally run or programmed either the Universal or the Fuji to any great extent, I have worked in factories that have utilized each type. One had 4796 machines and the other used Fuji CP3, 4, 4-2, 6, 643. As an observer I am d
Electronics Forum | Fri Dec 01 12:02:15 EST 2000 | blnorman
I have over 10 years experience in aerospace materials, part of which was involved with vacuum casting inert propellant formulations. These propellants are in the range of 80 - 90% solids loaded with viscosities of 15 kP. I'm not sure where I could
Electronics Forum | Tue Oct 27 10:15:54 EST 1998 | Chrys
| We have installed a Sonoflux atomized mist fluxing unit (Model 9500)on our Future 1 wave solder machine. We are concerned that the retrofitting of this unit may not have been appropriate for our equipment, as we are now experiencing many problems
Electronics Forum | Tue Mar 03 16:14:37 EST 2015 | lokit
Hello, No experience with Mirtec, they are more populair in the States and Asia it seems. For my company, not only the inspection depth and reducing false fails was important, but also good costumer support. Keep in mind that if you have problems w
Electronics Forum | Thu Jun 07 14:17:55 EDT 2007 | mfgengr
Thank you ChrisW. I agree completely. The decision to idle the temperature or turn the wave off is primarily a function of machine utilization. Period. The utilization % break even point for idle vs. turning the heat off is calculated by comparing th
Electronics Forum | Fri Jan 13 02:54:25 EST 2017 | roblackey
When the YV100 starts up if you press a key > during its startup you can get it to ascreen > where it asks for passwords.. > > How would you > get the passwords from this Hi, if you haven't changed them then I think it's "specialist" on VIOS.
Electronics Forum | Wed Nov 29 10:50:24 EST 2000 | blnorman
Vacuum casting (same process used to make solid rocket motors) should remove any air from the paste. We had thought of pressurizing the tubes to remove the residual paste, but that would entrap air. The problem of tubes sitting out for different
Electronics Forum | Fri May 12 11:40:25 EDT 2006 | solderiron
If you can change to SN100C do it. The nickel prevents the high tin content from eating away at the metals on the tips. Similar to what the Lead did in 63/37 alloys. This Koki crap is just that, crap. 99% tin??? Thats what is causing the problem peop
Electronics Forum | Thu Dec 26 16:51:47 EST 2002 | davef
First, an earlier poster suggested using DI water. We are NOT excited about DI water with a NC fluxer, unless DI water is the proper flux thinner. Second, as you inplied, the maintenance steps you take should vary according to the amount of time th