Electronics Forum | Tue Mar 20 06:09:20 EDT 2007 | d0min0
Hi, can't find answer to my question on web - maybe someone can help would it be compatible to use a wire of Sn62Pb36Ag2 for a product made with Sn63Pb37 paste ??? regards
Electronics Forum | Wed Jan 03 18:44:13 EST 2001 | Todd Koeppel
If we procure parts with a Sn/Ag termination, can we still use standard Sn/Pb solder pastes and the current reflow and wave processes?
Electronics Forum | Tue Aug 14 21:51:29 EDT 2001 | mugen
true.... tata why the elongation% is there.....
Electronics Forum | Tue Mar 20 06:42:32 EDT 2007 | Elena
I think, it will be no problems, if there's no Bi in a covering of components.
Electronics Forum | Mon Aug 04 15:46:05 EDT 2014 | dyoungquist
What do you mean by "airborne"? We have been using SnPbAg for 15+ years to build assemblies to IPC class II standards although with most assemblies going to Pb free, we are not using it near as much as we used to.
Electronics Forum | Tue Nov 21 09:46:19 EST 2006 | jax
I assume you are talking about Sn62Pb36Ag2 solder. You should not see any added concerns when subjecting Sn62 to multiple reflow cycles as compared to Sn63. As compared to Sn63Pb37: Reduced leaching issues Increased Wetting due to lo
Electronics Forum | Mon Aug 04 23:25:28 EDT 2014 | madhuranatha
Let me thank you for the reply. We are manufacturing products which are fitted on the aircraft. We are using SN63Pb37 solder paste for PCB assembly. Of late one of the solder paste supplier recommended SnPbAg for better solder-ability & reliabi
Electronics Forum | Mon Aug 04 23:27:05 EDT 2014 | madhuranatha
Let me thank you for the reply. We are manufacturing products which are fitted on the aircraft. We are using SN63Pb37 solder paste for PCB assembly. Of late one of the solder paste supplier recommended SnPbAg for better solder-ability & reliabi
Electronics Forum | Thu Dec 09 09:29:24 EST 2004 | Joel Dudley
I'm hoping to find someone out there who has some no clean, 93.5 PB, 3 SN, 1.5 AG, .015 Diameter. If you have some and are willing to part with it please let me know.
Electronics Forum | Thu Dec 09 09:58:44 EST 2004 | davef
This is a perculiar alloy. Usually, the portions of each metal in the alloy sum to 100. Yours sums to 98. Could you be seeking 93.5Pb 5Sn 1.5Ag? It is more available.