Electronics Forum | Fri Mar 31 15:49:51 EST 2006 | GS
Hi Marcus, by using SN100C have you seen any tearing phenomena like what shown on the link ? http://www.smartgroup.org/pdf/Defect01.pdf Tnks Regards.........GS
Electronics Forum | Fri Nov 09 16:31:02 EST 2007 | dmunson
We are using SAC305 for reflow and SN100C for our selective solder.
Electronics Forum | Mon Jul 17 08:49:02 EDT 2006 | russ
Hi Paul, not to throw a wrench in here but I beleive that paople are talking about switching from SAC in wave to SN100C, NOT SACx, these are different. and should not be confused. SACx is supposed to fall somewhere in the middle of the SN100C and t
Electronics Forum | Fri Mar 31 12:27:27 EST 2006 | Marcus
We have used the SN100C for over a year now with fanastic results. We use the SAC305 for SMT and SN100C wire exclusively. There are no problem mixing the alloys. I am also on the commitee for the NASA testing. The SN100C did out perform SAC and SnPb
Electronics Forum | Thu May 25 19:21:58 EDT 2006 | grantp
Hi, So that's really important to have a specific flux for lead free? We are looking at changing to SN100C after reading this thread and other stuff we have found, so can anyone recommend the best no clean flux for that metal? Do you need differen
Electronics Forum | Wed Sep 04 07:15:02 EDT 2013 | anilw2006
We have using SAC305 type solder paste for lead free process. One sample paste received of SN100C.After reflow SN100C type paste joint looks brighter and good compare to SAC305. Please help me which paste is good for smt process?
Electronics Forum | Mon Jan 02 08:54:58 EST 2006 | aj
has anyone used or trialed the SACX from Alpha, from reportes and studies carried out it seems that its a go between SAC305 and SN100.
Electronics Forum | Wed Jul 27 17:18:07 EDT 2005 | Carl
Any issues in your experience using SAC305 for reflow and SN100C for wave on ENIG pcbs? I've seen the CD, but there's not much specific data regarding ENIG pcbs Thanks
Electronics Forum | Thu Dec 29 09:20:30 EST 2005 | Cmiller
We have tested SN100C and SAC305 in our selective solder machine (Ersa Versaflow). We wanted to test both alloys in the selective first because the investment in filling the pots is minimal. In our initial tests the SN100C alloy appears to be the bes
Electronics Forum | Thu Dec 29 11:54:31 EST 2005 | Cmiller
We bought the lead free pots for the Ersa machine and change back and forth. We had a lot of problems running SAC305 in the Ersa. It seems to create a ton of dross and you need to frequently clean and flux the nozzles. I would really like some feed