Electronics Forum | Tue Dec 01 07:24:44 EST 1998 | Earl Moon
| Hi folks , | Lately we are seeing a lot of rawcards with black spots on the pads - most of them have Au finish(immersion gold) . We did a lot of inspecton after wave solder and found that only (fine pitch) QFP are affected the most. Our inspection
Electronics Forum | Tue Dec 01 07:54:49 EST 1998 | kallol chakraborty
| | Hi folks , | | Lately we are seeing a lot of rawcards with black spots on the pads - most of them have Au finish(immersion gold) . We did a lot of inspecton after wave solder and found that only (fine pitch) QFP are affected the most. Our inspec
Electronics Forum | Mon Jun 28 10:03:22 EDT 2004 | davef
First, welcome to your new job. Second, IPC-TM-650 2.6.14 is only loosely an �Ionic Contamination (Electromigration) Test�. * Electromigration Test, IPC TM 650 2.6.14, 2.6.14.1 * Ion Chromatography for Ionic Cleanliness, IPC TM 650 2.3.28 Third, I
Electronics Forum | Fri Sep 17 15:01:05 EDT 1999 | Dave F
| | We have some SMT components with gold plated leads. They're actually LCC led packages. A good solder alloy to use would be Indium / Lead to reduce tin dissolution into the gold and avoid the resultant brittle intermetallic compound. However, a re
Electronics Forum | Fri Sep 17 09:54:40 EDT 1999 | Brian
| | | We have some SMT components with gold plated leads. They're actually LCC led packages. A good solder alloy to use would be Indium / Lead to reduce tin dissolution into the gold and avoid the resultant brittle intermetallic compound. However, a
Electronics Forum | Fri Sep 17 10:09:17 EDT 1999 | Earl Moon
| | | | We have some SMT components with gold plated leads. They're actually LCC led packages. A good solder alloy to use would be Indium / Lead to reduce tin dissolution into the gold and avoid the resultant brittle intermetallic compound. However,
Electronics Forum | Fri Apr 07 17:17:55 EDT 2000 | Dave F
Ashok: You should select and use low residue tapes. But ya know, ya go out and research a great tape and if yer not careful, the buyer will second source ya and (surprise) ya got residues again. We have found that Lemme say this about Katon tape
Electronics Forum | Fri Sep 22 16:21:31 EDT 2006 | patrickbruneel
Figure 1. Human Toxicity Potential, Life-cycle Comparison Tin/lead solder paste is the top formula. SAC is second from the bottom.3 RoHS Report Excludes Comparisons By George A. Riley, contributing editor A European Union (EU) Commission for Envir
Electronics Forum | Wed Jul 14 11:36:56 EDT 1999 | Jimmy Strain
| | | Hi All, | | | Does any one experienced the solder on gold finger after | | | reflow. Its about 5 to 8 mils diameter . | | | We'd clean the entire screen printer, mounter & reflow as well, | | | but doesn't help much. | | | | | | | | Mr Kong..
Electronics Forum | Wed May 05 03:57:00 EDT 1999 | Bernard Mulcahy
| Hi Ya' John! | | Here's my comeback to the points you've raised...you knew I would have a comeback, didn't ya'? | | |Steve, | | | | I see your point, and yes there are alot bigger fish to fry in |the removal or control of lead in the environment